1) formed conductor
成形导体
2) forming rail
成形导轨
3) shaped conductor
成型导体
4) sector conductor
扇形导体
1.
Reduction of the production costs of 3-core XLPE cable by use of sector conductors;
采用扇形导体降低三芯交联电缆的制造成本
2.
6/1kV sector conductor Si-XLPE cables is analysed and investigated.
6/1kV硅烷交联聚乙烯绝缘电缆采用扇形导体的成缆工艺进行分析和探讨,并且对硅烷交联聚乙烯绝缘电缆采用圆形导体与扇形导体的经济性进行了比较。
5) conductor bar
棒形导体
1.
This paper analyzes the characteristics of the electric field produced by a limited long linear charge of electricity, and in the light of the principle the solution of a static electric field is single, an eggshaped conductor s electric potential and capacitance are calculated by using an equivalent charge and aconductor bar s capacitance is approximately obtained.
分析了有限长线电荷周围的电场分布 ,进一步根据静电场解的唯一性定理 ,对带有电荷的椭球状导体的电位和电容利用等效的线电荷进行了分析 ,而且 ,还对实际的棒形导体的电容进行了近似计算。
6) conducting rectangle
矩形导体
1.
An efficient numerical solution is presented for radar cross section from conducting rectangles.
提出了一种用傅里叶级数作为导体表面感应电流的全域基函数计算电场积分方程，去求解矩形导体雷达散射截面的解法。
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。