1) glide twin
滑动双晶
2) twin gliding
双晶滑动
3) glide twin
滑移双晶
4) grain boundary sliding
晶界滑动
1.
It's obtained that main mechanism of superplastics is grain boundary sliding.
据此得出超塑性变形的主要机制是晶界滑动、孔洞和位错运动松弛晶界引起应力集中，协调了晶界滑动的连续进行。
2.
Microstructural observations suggest that grain boundary sliding (GBS) makes a substantial contribution to the superplastic deformation, and the.
显微组织观察和断口分析表明 ,工业态AZ31镁合金超塑变形主要由晶界滑动机制所控制 ,同时 ,动态再结晶也是合金超塑变形的一种协同机制。
3.
Its main mechanism of superplasticity deformation is grain boundary sliding,and the main r.
Ti3Al金属间化合物超塑变形的主要机制是晶界滑动,失效的主要原因是空洞的形成和连接。
5) intracrystalline slip
晶内滑动
6) grain boundary slip
晶界滑动
1.
Contrary to be crack sources and make mechanical properties of alloys deteriorate as it has been always considered, η phase was found to have little effect on room temperature properties and furthermore, it improved the high temperature ductility of the alloy via blocking the grain boundary slip due to it.
通过对一种Fe-Ni-Cr合金进行过时效后晶界上析出η相的研究发现,由于晶界η相与合金基体保持共格关系,η相对合金的室温性能影响不大;并且在高温变形条件下η相形成凸起,阻碍晶界滑动,减小在晶角处的应力集中,从而提高合金的高温塑性。
补充资料：晶界滑动
晶界滑动
grain-boundary slip
J 1 ngJle huadong晶界滑动(grain一boundary slip)高温下多晶体金属相邻晶粒在切应力作用下沿着晶粒间界的相对移动。高温下多晶体晶粒间界处的结合显著削弱，当受切应力作用时，晶粒发生沿着间界作相对的滑动而变形。晶界滑动速度相当缓慢，只有在蠕变条件下即温度高和应力低的情况下才显得重要。晶粒越小，单位体积内晶界面积越大，晶界滑动的作用就越大，即对总变形量的贡献就越大。作晶界滑动时，通常总需要晶粒内有一定数量的位错运动与扩散塑性变形;因为大多数晶粒形状不规则，为了发生晶界滑动时不产生裂口，晶粒形状必须作相应的变化，位错运动是满足这种要求的主要途径。材料然加工时发生断裂的主要原因是，晶界滑动时在三晶粒交界处造成的应力集中使该处产生楔形裂口(见图)，然后受张应力作用而沿晶界扩展导致断裂。卜卜芳卜升必才 楔形裂口形成示意图 (王祝堂)