1) lead germanate vanadate crystal
锗钒酸铅晶体
2) lead germanate single crystal
锗酸铅单晶
3) bismuth germanate crystal
锗酸铋晶体
1.
The etching morphology of bismuth germanate crystals grown by Bridgmanmethod were inverstigated.
研究了坩埚下降法生长锗酸铋晶体(BGO)的腐蚀形貌,比较了{112}、{111}、{110}、{100}晶面族的腐蚀形貌特征和速度,利用 X 射线劳厄定向并借助于极图确定了腐蚀坑的结晶学方位,推测了蚀坑的组成晶面主要是{112},其次是{110}。
4) Tungstovanadogermanic acid
钨钒锗酸
6) YVO 4 crystal
钒酸钇晶体
1.
The XRD experiments showed that the change of the pH results in different width of XRD lines of YVO 4 crystals for which the material were obtained by the same stoichiometric ratio.
用XPS证明钒酸钇晶体颜色加深以及晶体内部存在的包裹体与形成低价钒酸盐有关。
2.
The unpolarized axial and transverse optical absorption spectrum of Ho 3+ ions in YVO 4 crystal are measured, from which the strength of absorption transition oscillator is obtained.
分别测量了室温下光垂直、平行c轴入射时Ho3+ 掺杂钒酸钇晶体的非极化光吸收谱 ,得到Ho3+ 吸收跃迁振子强度的实验值 。
补充资料:锗酸铋晶体
分子式:Bil2GeO20;Bi4Oe3O12;Bil4GeO23
CAS号:
性质:等多种同素异构体。其中Bi4Ge3O12为立方晶系,点群43m。熔点1050℃。在可见光、X射线、γ和α射线的激发下可产生荧光。激发光谱305nm,荧光光谱480~510nm,光输出温度系数-1%/℃,临界能量10.5MeV。具有良好的闪烁性能,不吸潮、抗冲击,易于加工,化学性能稳定,不存在因掺杂不均引起的发光强度不均匀问题。有效原子系数高,荧光衰减时间短,有利于快速计算。用提拉法或下降法在大气气氛下生长。为高能射线的闪烁探测材料,用于正负电子对撞机。
CAS号:
性质:等多种同素异构体。其中Bi4Ge3O12为立方晶系,点群43m。熔点1050℃。在可见光、X射线、γ和α射线的激发下可产生荧光。激发光谱305nm,荧光光谱480~510nm,光输出温度系数-1%/℃,临界能量10.5MeV。具有良好的闪烁性能,不吸潮、抗冲击,易于加工,化学性能稳定,不存在因掺杂不均引起的发光强度不均匀问题。有效原子系数高,荧光衰减时间短,有利于快速计算。用提拉法或下降法在大气气氛下生长。为高能射线的闪烁探测材料,用于正负电子对撞机。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。