1) decomposition by fusion
熔融分解法
2) alkali melt decomposition
碱熔融分解
3) melt phase-separation
熔融分相法
1.
Nanometer TiO_2 photocatalytic material was prepared by melt phase-separation,the samples of TiO_2 were characterized with XRD,SEM,TEM and testing of photocatalytic capability were made using sewerage being a degradation material.
利用熔融分相法制备了纳米TiO_2光催化村料,用XRD,SEM,TEM技术对其结构进行了表征,并进行了光催化降解污水的实验。
2.
Nanometer TiO2 photocatalytic material was prepared by melt phase-separation.
实验采用了熔融分相法制备纳米TiO_2光催化材料,本文研究了该制备方法的实验原理,采用D T A,X R D,SEM,TEM等测试手段对实验结果进行分析,并对不同条件下热处理样品的T iO_2晶体的析晶情况进行讨论,用甲基橙作为模拟降解物进行光催化性能的测试。
4) decompose samples by melting
熔融分解试样
5) hot dispersion-ultrasonic technique
熔融超声分散法
1.
Method: To prepare solid lipid nanoparticles(SLN) loaded with Xionggui powder-supercritical carbon dioxide fluid extraction(XG-CO_2-SFE) using a hot dispersion-ultrasonic technique,establishing the best prescription of XG-CO_2-SFE-SLN through orthogonal design methods using entrapment efficiency of nanoparticles as index,and investig.
方法:采用熔融超声分散法制备芎归散超临界CO2萃取物固体脂质纳米粒混悬液,以包封率为考察指标,采用正交试验筛选最佳处方,并考察其物理化学性质;采用动态透析法考察其在不同介质中的释药特性。
6) melt
[英][melt] [美][mɛlt]
熔化，熔解，熔融;熔态;熔液
补充资料：为再结合熔融石英制品、熔融石英陶瓷制品
分子式：
CAS号：
性质：又称为再结合熔融石英制品、熔融石英陶瓷制品或石英玻璃烧结制品。具有良好的化学稳定性。抗酸性和抗冲刷性强。高温机械强度大。热膨胀系数低。气孔率低。导电率低。但在1100℃以上长期使用时，制品中的石英会向方石英转变，使制品产生裂纹和剥落。以熔融石英为原料，经粉碎、成型、干燥、烧成而制得。制法有泥浆浇注法、蜡注法、捣打法、半干压法和等静压成型等。由于在烧成时收缩小，可以制得尺寸精确的制品。可用于制作耐酸容器、反应罐内衬耐酸部件等。冶金工业中用其制成浸入式水口，使用效果很好。
CAS号：
性质：又称为再结合熔融石英制品、熔融石英陶瓷制品或石英玻璃烧结制品。具有良好的化学稳定性。抗酸性和抗冲刷性强。高温机械强度大。热膨胀系数低。气孔率低。导电率低。但在1100℃以上长期使用时，制品中的石英会向方石英转变，使制品产生裂纹和剥落。以熔融石英为原料，经粉碎、成型、干燥、烧成而制得。制法有泥浆浇注法、蜡注法、捣打法、半干压法和等静压成型等。由于在烧成时收缩小，可以制得尺寸精确的制品。可用于制作耐酸容器、反应罐内衬耐酸部件等。冶金工业中用其制成浸入式水口，使用效果很好。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条