1) hot impulse compacting
热冲击成形
2) shock forming
冲击成形
1.
Investigation of inverse deformation in laser shock forming with half die;
激光半模冲击成形中板料反向变形现象研究
2.
Several technologies called formative research profiles,focusing on technology of laser shock forming are introduced.
介绍了几种典型无模成形技术的研究概况,重点介绍了激光冲击成形的无模成形技术。
3.
Laser shock forming of metal sheet usually effects on the surface of workpiece in normal direction by laser beam,and produces shock wave force,which is vertical to the surface of workpiece.
在曲面板料激光冲击成形时,很难满足每次都能法向垂直冲击,因此非常有必要进行激光斜冲击板料研究。
3) rectangular thermal-shock
矩形热冲击
4) electrical impulse compacting
电冲击成形
5) Triangle Thermal Shock
三角形热冲击
6) hot stamping
热冲压成形
1.
Because of the differences between hot stamping and traditional cold stamping, the analysis of heat balance and temperature field is in urgency.
热冲压成形技术，是利用金属热塑性成形的原理，能够在成形的同时实现对板料的淬火热处理，提高材料的成形性能，大大扩展了高强度超高强度钢在汽车零件的应用范围。
2.
The hot stamping of martensitic steel blank is a n.
与传统的冷冲压工艺技术相比，热冲压成形工艺采用淬火性能更好的硼钢板为加工对象，能够在成形的同时实现对板料的淬火热处理，既利用了金属板料在高温下塑性提高的特点，同时又实现了对板料组织的淬火强化，并最终获得尺寸精度及机械强度俱佳的钣金制件。
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。