1) moulding
[英]['məʊldɪŋ] [美]['moldɪŋ]
膜压成型
2) rolling formation
轧膜成型
3) high pressure shaping
高压成型
1.
The technology of micro-structure controlling and strengthening under high pressure shaping of Al-Si series alloy is reviewed, and the industrialization of high pressure shaping domestically is also introduced.
综述了高压条件下的铝硅系列合金的晶粒组织控制及其强化技术,介绍了我国高压成型的产业化情况。
4) forming pressure
成型压力
1.
The influence of powder grain size and forming pressure upon the performance of W-Cu composites are discussed in this article.
研究了粉末粒度、成型压力及铜的损耗对钨铜复合材料制备的影响。
2.
The influence of powder grain size and forming pressure are discussed for the performance of W-Cu composites.
着重研究了粉末粒度与成型压力对钨铜材料烧结致密度的影响。
3.
Carbon fiber reinforced sulphoaluminate cement composites(CFSC) was fabricated by press moulding;the influence of forming pressure on smart properties of CFSC was studied.
采用压制成型方法,制备了碳纤维硫铝酸盐水泥基复合材料(carbon fiber rein-forced sulphoaluminate cement composites,简称CFSC),研究了成型压力对CFSC压阻效应和温阻效应的影响。
5) molding pressure
成型压力
1.
Influence of molding pressure and dunking time on the sulfate attack resistant nature of concrete
成型压力和浸泡时间对混凝土抗硫酸盐侵蚀性能的影响
2.
The effect of adding nano α-Al_2O_3 powder and molding pressure on microstructure and properties of micron-sized alumina ceramic was investigated.
为了解决氧化铝陶瓷脆性大、均匀性差等问题,我们在微米氧化铝粉体中添加一定比例的纳米-αAl2O3粉,研究纳米-αAl2O3粉的添加和成型压力对微米氧化铝陶瓷显微结构和性能的影响。
3.
During the process of the consolidation molding consolidation, this paper adopts three schemes to make kinds of samples, while it gives and studies the molding temperature as well as adopts the molding pressure, analyzing the relationship between the molding pressure and the molding thickness.
模塑成型的复合固化中,采用了三个方案复合出几种试样,并对试样的成型温度,成型压力的确定给予了探讨,同时分析了成型压力与成型厚度之间的关系。
补充资料：半干压成型
分子式：
CAS号：
性质： 坯料粒状粉末放入压力机的模具中压制成型的方法。粉料常采用喷雾干燥造粒，也可用过筛方法机械或手工造粒。粉料含水分一般为8%～14%。大都采用双面加压的成型机。制品收缩小、尺寸精确度较高，但模具要求较高，产品空隙率稍大，性能较差，不适于高压电瓷生产。对小件形状简单的制品比较适宜，且可连续成形，生产效率也较高。对于瘠性物料通常在造粒时加入适当的有机粘接剂，以保证成形坯体有足够的生坯强度。
CAS号：
性质： 坯料粒状粉末放入压力机的模具中压制成型的方法。粉料常采用喷雾干燥造粒，也可用过筛方法机械或手工造粒。粉料含水分一般为8%～14%。大都采用双面加压的成型机。制品收缩小、尺寸精确度较高，但模具要求较高，产品空隙率稍大，性能较差，不适于高压电瓷生产。对小件形状简单的制品比较适宜，且可连续成形，生产效率也较高。对于瘠性物料通常在造粒时加入适当的有机粘接剂，以保证成形坯体有足够的生坯强度。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条