2) chilled cast iron
冷激铸铁
1.
In order to eliminate the high content of ferrite structure in the outer layer with depth of 1 mm of the chilled cast iron camshaft produced in shell mould,an experiment with adding metal antimony into iron melt was conducted.
为消除用覆膜砂壳型铸造工艺生产的冷激铸铁凸轮轴主轴颈外表面1 mm左右深度内的大量铁素体组织,进行了在铁液中加入金属锑的试验,加入量(质量分数)分别为:0。
2.
The "black line" defect found on chilled cast iron camshafts was analyzed metallographically and found that the microstructure of defect zone consisted of pearlitic matrix and D-type graphite.
对冷激铸铁凸轮轴的"黑线"缺陷进行显微分析发现,缺陷区的基体组织为珠光体,石墨形态为枝晶点状石墨。
3) Controlled-casting and controlled-cooling
控铸控冷
4) Water-cooling cast
水冷浇铸
5) DC casting
直冷铸造
6) Chilled iron
激冷铸铁
1.
In room temperature,under load and continuous lubrication condition, malleable iron,wear resistant iron,naduar iron,chilled iron with 45 # steel can be employed;chilled with wear resistant iron;chilled with chilled iron comparative testing research friction-wear characteristics of chilled iron.
在室温、载荷及连续润滑条件下 ,用可锻铸铁、耐磨铸铁、球墨铸铁、激冷铸铁与 4 5 # 钢 ,激冷铸铁与耐磨铸铁 ,激冷铸铁与激冷铸铁对磨试验 ,研究了激冷铸铁的摩擦磨损性能 结果表明 ,激冷铸铁的摩擦系数与磨损量均小于可锻铸铁与耐磨铸铁 ,其摩擦系数波动在 0 。
补充资料：冷激
分子式：
CAS号：
性质：又称骤冷。在多层固定床绝热反应器中进行放热反应时，在催化剂层间注入冷的原料，与高温的反应物混合，以直接换热的方式降低反应物的温度，称为冷激。反应物通过一层催化剂产生一定的绝热温升后进入下一层前，冷的原料与该反应物充分混合(冷激)后再进入下一层催化剂进行反应，以降低进入下一层催化剂的入口温度。
CAS号：
性质：又称骤冷。在多层固定床绝热反应器中进行放热反应时，在催化剂层间注入冷的原料，与高温的反应物混合，以直接换热的方式降低反应物的温度，称为冷激。反应物通过一层催化剂产生一定的绝热温升后进入下一层前，冷的原料与该反应物充分混合(冷激)后再进入下一层催化剂进行反应，以降低进入下一层催化剂的入口温度。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条