1) polystyrene-born tribromide
聚苯乙烯三溴化硼
2) Poly-tribromostyrene
聚三溴苯乙烯
3) brominated polystyrene
溴化聚苯乙烯
1.
Determination of bromine content in brominated polystyrene;
溴化聚苯乙烯中溴含量的测定
2.
With polystyrene(PS) and bromine as raw materials,AlCl3 as catalyst,CH2Cl2 as solvent,the brominated polystyrene(BPS) flame retardant was synthesized.
采用原子转移自由基聚合(ATRP)法合成低相对分子质量、相对分子质量分布较窄的聚苯乙烯(PS),以PS、Br2为原料,AlCl3作催化剂,CH2Cl2为溶剂,低温反应5～6h合成低相对分子质量溴化聚苯乙烯(BPS),用于对PA6进行阻燃。
3.
A method was investigated for preparing brominated polystyrene by the interaction between low molecular polystyrene and bromine chloride in 1,2-dichloroethane in the presence of AlCl3 and under almost anhydrous condition.
简述在二氯乙烷溶剂中，以路易斯酸三氯化铝为催化剂，在近似无水条件下，聚苯乙烯与氯化溴反应制备溴化聚苯乙烯的方法。
4) polybromostyrene
聚溴化苯乙烯
1.
The effect of polybromostyrene(PBS)content on the flame retardance and mechanical properties of glass fiber reinforced nylon 6(PA6)was investigated.
研究了聚溴化苯乙烯(PBS)对玻纤增强尼龙6(PA6/GF)阻燃和力学性能的影响,并采用锥形量热仪研究了改性水滑石(HT)对PBS/Sb2O3阻燃PA6/GF抑烟作用和燃烧时热释放速率的影响。
2.
The effect of polybromostyrene (PBS) content on the flame-retardancy and mechanical properties of glass fiber reinforced nylon 6 (PA6/GF) was investigated.
研究了聚溴化苯乙烯(PBS)对玻纤增强尼龙6(PA6/GF)阻燃和力学性能的影响,并采用锥形量热仪研究了改性水滑石(HT)对PBS/Sb_2O_3阻燃PA6/GF的抑烟作用和燃烧时热释放速率的影响。
5) poly(tribromostyrene)
均聚(三溴乙烯苯)衍生物
6) Bromotriphenyl ethylene
三苯溴乙烯
补充资料：聚苯乙烯/聚乙烯共混物
分子式：
CAS号：
性质：由聚苯乙烯与聚乙烯系列为主组成的共混物，添加少量第三组分，如氢化丁苯嵌段共聚物或接枝共聚物等作增容剂，既有聚苯乙烯良好的成型加工性和刚性，又改善其脆性、应力开裂及耐油性，例如：80份聚苯乙烯与20份聚乙烯共混，加入10份氢化丁苯热塑性弹性体，冲击强度可达36.7kJ/m2，拉伸强度为20.8MPa，可通过机械共混或反应挤出共混制备，用于含油脂较多的食品包装容器，如乳制品包装等方面。
CAS号：
性质：由聚苯乙烯与聚乙烯系列为主组成的共混物，添加少量第三组分，如氢化丁苯嵌段共聚物或接枝共聚物等作增容剂，既有聚苯乙烯良好的成型加工性和刚性，又改善其脆性、应力开裂及耐油性，例如：80份聚苯乙烯与20份聚乙烯共混，加入10份氢化丁苯热塑性弹性体，冲击强度可达36.7kJ/m2，拉伸强度为20.8MPa，可通过机械共混或反应挤出共混制备，用于含油脂较多的食品包装容器，如乳制品包装等方面。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。