1) solid-to-liquid ratio
固液比<冶>
2) solid-liquid mixing
固-液混合<冶>
3) solid-liquid interface
固液界面<冶>
4) liquid-solid absorption
液固吸附<冶>
5) solid-to-liquid ratio
固液比
1.
The effects of temperature, dialogite-to-sulfuric acid ratio, and solid-to-liquid ratio on leaching of dialogite by sulfuric acid were researched in the leaching experiment of ores from Hubei.
通过对湖北矿的浸取试验研究,讨论了温度、矿酸比、固液比对菱锰矿硫酸浸取的影响,优化了浸取条件,并确定温度对浸取的影响最为显著,使浸取率可以达到99。
2.
Solid-to-liquid ratio is introduced to estimate the solid-like of microstructure.
为揭示超薄膜的摩擦特性与微观结构的关系,运用分子动力学模拟的方法对其进行研究,采用固液比作为流体膜固化的定量描述,分别讨论温度、分子层数对固液比和摩擦力的影响。
3.
The result shows that the properties of geopolymer are the best when the containing of metakaolin in the solid phase is 25%,the containing of water glass in the liquid phase is 65%,solid-to-liquid ratio is 3.
结果表明:当偏高岭石占固相含量为25%,水玻璃占液相的含量为65%,固液比为3。
6) solid-to-solution ratio
固/液比
1.
The influence of solid-to-solution ratio(SSR) on the sorption and desorption of dissolved petroleum hydrocarbons(DPH) to two surface soils(agricultural and black) was evaluated by batch reactor experiments.
采用批实验的方法,研究了2种土壤在不同的固/液比(solid-to-solution ratio,SSR)条件下对溶解性石油烃(DPH)的吸附-解吸特性。
补充资料：液固比
液固比
liquid-solid ratio
yegub-液固比(liquid一solid ratio)矿浆中水溶液质量与固体物料质量的比值。是湿法冶金浸出过程一个重要的技术经济参数。在一定的浸出剂浓度下，大的液固比可降低矿浆的粘稠度和浸出液中有价金属离子浓度，有利于提高固液相之间的传质速度，从而有可能提高浸出率。但液固比过大会导致浸出和液固分离设备负荷或浸出剂的损耗增加，在经济上未必有利。因此，最佳的液固比值，往往需要通过试验研究确定。 (鲁君乐)