1) high temperature setting glue
高温固化胶
2) high temperature curing
高温固化
1.
The application of the process of high temperature curing in VRLA battery;
高温固化在VRLA电池中的应用
2.
Mechanism and effect of unformed plate of high temperature curing on the performance of valve-regulated lead-acid(VRLA) battery were elaborated, effect of curing temperature on the curing quality of plates and the performance of batteries were also discussed.
综述了铅酸蓄电池生产中生极板高温固化的机理和作用,以及固化温度对极板固化质量和电池性能的影响,得出采用高温固化的关键是3PbO·PbSO4(3BS)向4PbO·PbSO4(4BS)转化,4BS铅膏的生成和腐蚀层改善了板栅/正极活性物质(PAM)界面的连接性能的结论。
3) low-temperature setting glue
低温固化胶
4) room temperature setting adhesives
室温固化胶
5) high temperature and heavy wet solidification
高温高湿固化
1.
A high temperature and heavy wet solidification process is taken to make plate, fast cycle life was improved by 25%.
极板采用高温高湿固化工艺,快速循环寿命可提高约1/4。
6) Temperature dependent hydrogel
温固化水凝胶
1.
The experimental study on bone marrow stromal cells loaded temperature dependent hydrogel on repair of full-thickness defects of rabbit articular cartilage;
温固化水凝胶负载骨髓基质干细胞修复兔关节骨软骨缺损的实验研究
补充资料：高温固化树脂基复合材料
分子式：
CAS号：
性质：在高温下固化成型的树脂基复合材料。高温一般指高于150℃的温度。常用的树脂有酚醛和环氧树脂。前者包括两类：热塑性酚醛树脂采用六亚甲基四胺(乌洛托品)固化剂，固化温度为150～170℃；热固性酚醛树脂的固化温度为160℃。酚醛树脂的高温固化需在高压下进行。环氧树脂高温固化剂有芳香胺，如DDM、DDS、MPSA、二元酸酐，如顺丁烯二酸酐、邻苯二酸酐和双腈胺等。这类复合材料基体树脂结构紧密，热稳定性好、强度高、耐化学腐蚀性和耐大气老化性能优良，并且预浸料具有较长的适用期。工艺条件复杂，需高温加热设备，对大型制件难以满足，应在保证性能前提下尽量降低固化温度，靠近中温固化。适用于制造有较高使用温度要求的非大型结构件，广泛用于航空航天、机械制造、能源、化工及其他工业领域。
CAS号：
性质：在高温下固化成型的树脂基复合材料。高温一般指高于150℃的温度。常用的树脂有酚醛和环氧树脂。前者包括两类：热塑性酚醛树脂采用六亚甲基四胺(乌洛托品)固化剂，固化温度为150～170℃；热固性酚醛树脂的固化温度为160℃。酚醛树脂的高温固化需在高压下进行。环氧树脂高温固化剂有芳香胺，如DDM、DDS、MPSA、二元酸酐，如顺丁烯二酸酐、邻苯二酸酐和双腈胺等。这类复合材料基体树脂结构紧密，热稳定性好、强度高、耐化学腐蚀性和耐大气老化性能优良，并且预浸料具有较长的适用期。工艺条件复杂，需高温加热设备，对大型制件难以满足，应在保证性能前提下尽量降低固化温度，靠近中温固化。适用于制造有较高使用温度要求的非大型结构件，广泛用于航空航天、机械制造、能源、化工及其他工业领域。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。