1) bakelite B,resite,
酚醛树脂 B
2) fire-resistant resin
B改性酚醛树脂
3) B-stage resin
B阶树脂
4) PF resin
酚醛树脂
1.
The development of wood PF resin adhesive;
木材工业用酚醛树脂胶粘剂的现状及研究进展
2.
Special PF Resin for Light-alloy Coated Sand;
轻合金覆膜砂专用酚醛树脂的开发研究
3.
Using pyrolytic tar from larch bark as partial substitute for phenol in proportions of 0%, 20%, 40%, 60% , four types of PF resins were prepared and applied in hot-pressing three- layer poplar plywood by orthogonal test methods with different levels of press pressure, press time, and and resin content.
以落叶松树皮热解油按比例0%、20%、40%、60%代替苯酚制备的4种酚醛树脂胶黏剂和人工林杨木单板为原料,采用正交实验设计方法,选择不同的热压压力、热压时间和涂胶量进行了3层胶合板压制试验。
5) phenol-formaldehyde resin
酚醛树脂
1.
Investigation on curing mechanism of phenylphenol modified phenol-formaldehyde resin by means of DSC method;
DSC对苯基苯酚改性酚醛树脂固化机理研究
2.
Preparation of water-soluble low hydroformylation phenol-formaldehyde resin;
一种低甲醛含量水溶性酚醛树脂的制备
3.
Preparation of phenol-formaldehyde resin/graphite bipolar plate conductive composite of high properties;
高性能酚醛树脂/石墨双极板导电复合材料的制备
6) Phenol formaldehyde resin
酚醛树脂
1.
Study on modified phenol formaldehyde resin adhesive with pulping waste liquor;
木质素改性酚醛树脂胶的研究
2.
Study on urea-modified phenol formaldehyde resin adhesive;
尿素改性酚醛树脂胶粘剂的研究
3.
Study of polyurethane modified phenol formaldehyde resin;
聚氨酯改性酚醛树脂的研究
补充资料：2401纯酚醛树脂
2401树脂是由烷基苯酚和甲醛在碱性介质下缩聚而制得。有优良的耐热性、耐磨性、耐水性和耐老化性等。溶于苯、甲苯、醋酸乙酯、溶剂汽油、环己烷等有机溶剂和植物油。240l树脂的质量规格与2402完全相同。与氯丁橡胶和丁腈橡胶有良好的相容性。
外观 黄色至棕红色透明块状固体
软化点(环球法) 80-110 ℃
油溶性(树脂：桐油＝1：2) 全溶
用作氯丁胶粘剂的增粘树脂，以该树脂配制的氯丁溶剂型胶粘剂，粘接铝帆布的剥离强度达4kN／m。还可用作压敏胶的增粘剂、丁基橡胶的硫化剂等。贮存于阴凉、通风的库房内，远离火种、热源。
外观 黄色至棕红色透明块状固体
软化点(环球法) 80-110 ℃
油溶性(树脂：桐油＝1：2) 全溶
用作氯丁胶粘剂的增粘树脂，以该树脂配制的氯丁溶剂型胶粘剂，粘接铝帆布的剥离强度达4kN／m。还可用作压敏胶的增粘剂、丁基橡胶的硫化剂等。贮存于阴凉、通风的库房内，远离火种、热源。