1) plasma arc heater
等离子弧加热器<冶>
2) plasma arc heater
等离子弧加热器
1.
A plasma arc heater has been developed,whose plasma arc could be ignited simply,which can work steadily for a longer time,and whose power could be regulated expediently.
研制了一种等离子弧加热器,它具有引弧快捷、连续工作时间长、功率调节方便的优点,可以应用于电站锅炉等离子弧无油点火、助燃,煤化工的热源,垃圾焚烧,化学气相沉积等领域。
3) Arc plasma heater
电弧等离子体加热器
4) thermal-plasma arc
热等离子弧
1.
Ni-based alloy was clad on Q235 substrate by use of the thermal-plasma arc cladding method.
运用热等离子弧熔覆法,在Q235基体表面熔覆了镍基合金,对合金的组织和形成原因及熔覆层和基体的界面进行了分析研究。
5) thermal plasma arc
热等离子弧
1.
A coating of Stellite Ni60 material,which is a commercial nickel base self melting alloy powder,was melting plated on Q235 steel surface by using thermal plasma arc.
用热等离子弧在Q 235钢基体表面熔覆材料为Stellite N i60商用镍基自熔性合金粉的涂层,涂层厚1 mm。
2.
The cladding layer of Stellite Ni60 alloy powder has been prepared on Q235 steel with thermal plasma arc equipment.
利用热等离子弧熔覆装置在Q235钢表面熔覆Stellite Ni60合金粉末。
6) plasma heating device
等离子体加热器
补充资料：等离子弧焊
利用等离子弧作为热源的焊接方法（见图）。气体由电弧加热产生离解，在高速通过水冷喷嘴时受到压缩，增大能量密度和离解度，形成等离子弧。它的稳定性、发热量和温度都高于一般电弧，因而具有较大的熔透力和焊接速度。形成等离子弧的气体和它周围的保护气体一般用氩。根据各种工件的材料性质，也有使用氦或氩氦、氩氢等混合气体的。等离子弧有两种工作方式。一种是"非转移弧"，电弧在钨极与喷嘴之间燃烧，主要用于等离子喷镀或加热非导电材料；另一种是"转移弧"，电弧由辅助电极高频引弧后，电弧燃烧在钨极与工件之间，用于焊接。形成焊缝的方式有熔透式和穿孔式两种。前一种形式的等离子弧只熔透母材，形成焊接熔池，多用于0.8～3毫米厚的板材焊接；后一种形式的等离子弧只熔穿板材，形成钥匙孔形的熔池，多用于 3～12毫米厚的板材焊接。此外，还有小电流的微束等离子弧焊,特别适合于0.02～1.5毫米的薄板焊接。等离子弧焊接属于高质量焊接方法。焊缝的深／宽比大，热影响区窄，工件变形小，可焊材料种类多。特别是脉冲电流等离子弧焊和熔化极等离子弧焊的发展，更扩大了等离子弧焊的使用范围。