1) fluorovinyl ether
[化]氟乙烯基醚
2) hyl vinyl ether
三氟乙基乙烯醚
3) fluroxene
氟乙烯醚
4) 2,2,2-trifluoroethyl vinyl ether
2,2,2-三氟乙基乙烯基醚
5) perfluoroalkyl vinyl ether
全氟代烷基乙烯基醚
1.
Performance and synthesis methods of perfluoroalkyl vinyl ether, non- aqueous solution polymerization and aqueous solution polymerization processes of tetrafluoroethylene- perfluoroalkyl vinyl ether copolymer are reviewed.
介绍了全氟代烷基乙烯基醚的物性和合成方法;叙述了四氟乙烯与全氟代烷基乙烯基醚共聚物非水溶液、水溶液聚合工艺。
6) trifluorovinyl aryl ether
三氟乙烯基芳基醚
1.
A series of trifluorovinyl aryl ethers were synthesized by dehalogenation of 2 bromo 1,1,2, 2 tetrafluoroethyl aryl ethers which were prepared from the reaction of the corresponding phenoxides with 1,2 dibromo 1,1,2,2 tetrafluoroethane in tetraglyme.
三氟乙烯基芳基醚类聚合物具有优异的材料性能,可在高温润滑剂[1],LCD显示器中的介电层[2]等方面得到应用。
补充资料：四氟乙烯-全氟烷基乙烯基醚共聚纤维
分子式：
CAS号：
性质：指共聚有少量全氟烷基乙烯基醚的可熔聚四氟乙烯纤维。一般只作单丝，密度2.2g/cm3，强度1.46cN/dtex，伸长率9％-12％，沸水收缩率12％～15％。制法是将四氟乙烯和4.4％～7％(摩尔)的共聚单体进行游离基聚合，再将树脂在340～360℃熔纺和拉伸而得。用途主要作离子交换膜的补强织物和强度要求高的耐腐蚀材料。
CAS号：
性质：指共聚有少量全氟烷基乙烯基醚的可熔聚四氟乙烯纤维。一般只作单丝，密度2.2g/cm3，强度1.46cN/dtex，伸长率9％-12％，沸水收缩率12％～15％。制法是将四氟乙烯和4.4％～7％(摩尔)的共聚单体进行游离基聚合，再将树脂在340～360℃熔纺和拉伸而得。用途主要作离子交换膜的补强织物和强度要求高的耐腐蚀材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条