The master alloy ingot of Nb-Ti-Si based ultrahigh temperature alloy was prepared by vacuum nonconsumable arc melting.
采用真空非自耗电弧熔炼法制备Nb-Ti-Si基超高温合金的母合金锭,分别于1300、1400、1500和1600℃保温50h,对其进行均匀化处理,然后于1100℃保温50h进行时效处理。
3) Ti-Nb-Si based ultrahigh temperature alloy
Ti-Nb-Si基超高温合金
1.
Microstructures of Si-Cr co-depositing coatings prepared on Ti-Nb-Si based ultrahigh temperature alloy
Ti-Nb-Si基超高温合金Si-Cr共渗抗氧化涂层的显微组织
4) Nb-Ti-IF steel
Nb-Ti-IF钢
1.
According to the processes of continuous hot-dip galvanizing lines,an industrially hot rolled and cold rolled Nb-Ti-IF steel was used to study the effect of annealing processes on the microstructures and recrystalliza- tion textures.
以典型成分Nb-Ti-IF钢冷轧硬卷为研究材料,结合连续热镀锌线工艺特点,系统研究了退火工艺对试验钢组织和织构的影响。
5) microalloying Ti Nb steel
微Ti-Nb钢
补充资料：Nb-Ti alloy
分子式：
CAS号：
性质：由金属铌和金属钛所组成的合金。工业生产的铌钛合金，钛含量一般为20%～60%（质量），最典型的铌钛合金含钛66%[约50%（质量）]。它们是重要的合金型超导材料，其超导转变温度为8～10K，加入其他元素还可以进一步提高超导性能。钛在合金中以固溶体状态存在。合金用混合粉末烧结和铌片、钛片组成的电极经真空自耗电弧炉或电子束熔炼数次成合金锭。