1) alumina ceramics,95
氧化铝陶瓷95
2) 95% alumina ceramics
95%氧化铝陶瓷
3) alumina ceramics,95
氧化铝陶瓷,95
4) 95 alumina ceramics
95氧化铝瓷
1.
The rheological behavior of the slurry of 95 alumina ceramics for gelcasting was discussed in this paper.
本文研究95氧化铝瓷凝胶注模成型中浆料的流变性。
5) Alumina ceramics
氧化铝陶瓷
1.
Effects of sintering temperature on fatigue damage of alumina ceramics;
烧结温度对氧化铝陶瓷疲劳损伤过程的影响
2.
Quantitatively research of fatigue damage of alumina ceramics;
氧化铝陶瓷疲劳损伤过程的数字描述
3.
Application of steel-alumina ceramics composite pipe for dilute phase pneumatic conveying;
氧化铝陶瓷内衬复合钢管在稀相气力输送中的应用
6) alumina
[英][ə'lu:mɪnə] [美][ə'lumɪnə]
氧化铝陶瓷
1.
Dynamic behaviors of alumina ceramic under high pressure and high strain-rate;
氧化铝陶瓷在高压高率条件下动态特性
2.
Experimental study on shear response of alumina under combined compression and shear loading;
压剪复合冲击下氧化铝陶瓷的剪切响应实验研究
3.
The effect of different impurities and dopants on the dielectric loss of alumina ceramics are reviewed.
综述了不同杂质及掺杂对氧化铝陶瓷介电损耗影响的研究进展。
补充资料：氧化铝陶瓷95
分子式： Al2O3
CAS号：
性质：含量为95％(质量)的氧化铝陶瓷，主晶相为α-Al2O3，烧结温度在1650℃±20℃左右。主要性能：相对介电常数8.5～9.6，介电强度为15～18MV/m，体积电阻率1010～1012Ω·m，抗弯强度为280～350MPa，密度约3.5g/cm3。作为装置用陶瓷应用十分广泛。
CAS号：
性质：含量为95％(质量)的氧化铝陶瓷，主晶相为α-Al2O3，烧结温度在1650℃±20℃左右。主要性能：相对介电常数8.5～9.6，介电强度为15～18MV/m，体积电阻率1010～1012Ω·m，抗弯强度为280～350MPa，密度约3.5g/cm3。作为装置用陶瓷应用十分广泛。