1) fortified wash primer
长曝磷化底漆
2) phosphating primer
磷化底漆
1.
It were discovered from the result that corrosion-resistance of phosphating primer was still better by comparison with anoding chemical conversion film.
通过盐雾实验、稳态阳极极化曲线和电化学阻抗谱 3种测试方法 ,对磷化底漆和阿洛丁 (12 0 0 )化学转化膜进行了测试 ,结果发现磷化底漆的耐蚀性明显优于阿洛丁化学转化膜 。
2.
The findings show that corrosion resistance of phosphating primer is remarkably better than that of anoding chemical corrosion film:the polarization resistance(RP)of the former is an order higher in magnitude than the latter;the passive potential region of the former is from-0.
通过电化学阻抗谱和恒电位稳态阳极极化曲线2种电化学测试方法,对磷化底漆和阿洛丁化学转化膜进行了测试,发现磷化底漆的耐蚀性明显优于阿洛丁化学转化膜,其极化电阻RP比阿洛丁转化膜高一个数量级,钝化区电位范围在-0。
3) metal conditioner
金属处理剂;磷化底漆
4) zinc phosphate primer
磷酸锌底漆
1.
Performance and application of an anti corrosion system(zinc phosphate primer＋ polyurethane enamel)for oil tank external are introduced.
介绍了一种用于油罐外壁的防腐体系 (磷酸锌底漆＋工业聚氨酯磁漆 )的性能及应用前景。
5) phosphatizing top coat
磷化面漆
6) UV curable primer
UV固化底漆
补充资料：长曝磷化底漆
分子式：
CAS号：
性质：即增强洗涤底漆，是造船工业用车间底漆的一种。早期的磷化底漆防锈期限较短，只能防锈24h。长曝型磷化底漆则采用酚醛树脂增加固化，喷涂一道可达15～20μm厚，在室外曝露3个月不生锈。以酚醛改性的聚乙烯醇缩丁醛为基料，加入磷酸、铬酸锌、氧化铁红和体质颜料配制而成，分为一罐装和二罐装两种。其特点为室温干燥极快(3～5min)，附着力强，有一定的防锈性，钢板焊割时漆膜延燃性小，产生的气体对人体毒性低，适于钢板流水线高压喷涂，对船用钢板焊接质量和物理机械性能无不良影响，与多数有机防锈涂料匹配性好。
CAS号：
性质：即增强洗涤底漆，是造船工业用车间底漆的一种。早期的磷化底漆防锈期限较短，只能防锈24h。长曝型磷化底漆则采用酚醛树脂增加固化，喷涂一道可达15～20μm厚，在室外曝露3个月不生锈。以酚醛改性的聚乙烯醇缩丁醛为基料，加入磷酸、铬酸锌、氧化铁红和体质颜料配制而成，分为一罐装和二罐装两种。其特点为室温干燥极快(3～5min)，附着力强，有一定的防锈性，钢板焊割时漆膜延燃性小，产生的气体对人体毒性低，适于钢板流水线高压喷涂，对船用钢板焊接质量和物理机械性能无不良影响，与多数有机防锈涂料匹配性好。