It were discovered from the result that corrosion-resistance of phosphating primer was still better by comparison with anoding chemical conversion film.
通过盐雾实验、稳态阳极极化曲线和电化学阻抗谱 3种测试方法 ,对磷化底漆和阿洛丁 (12 0 0 )化学转化膜进行了测试 ,结果发现磷化底漆的耐蚀性明显优于阿洛丁化学转化膜 。
2.
The findings show that corrosion resistance of phosphating primer is remarkably better than that of anoding chemical corrosion film:the polarization resistance(RP)of the former is an order higher in magnitude than the latter;the passive potential region of the former is from-0.
通过电化学阻抗谱和恒电位稳态阳极极化曲线2种电化学测试方法,对磷化底漆和阿洛丁化学转化膜进行了测试,发现磷化底漆的耐蚀性明显优于阿洛丁化学转化膜,其极化电阻RP比阿洛丁转化膜高一个数量级,钝化区电位范围在-0。
补充资料：120固化剂
N-羟乙基乙二胺又称β-羟乙基乙二胺，俗称120固化剂，结构式H2N(CH2)2NH(CH2)2OH，分子量92．06。无色或淡黄色透明粘性液体，微有氨气味。呈强碱性。有吸湿性。与水、乙醇混溶，微溶于乙酸。能从空气中吸收二氧化碳。低毒．LD504032mg／kg。
用作环氧树脂的室温快速固化剂，参考用量16～18phr，固化条件RT／10h或80℃／3h。
贮存于阴凉、干燥的库房内，防潮。
用作环氧树脂的室温快速固化剂，参考用量16～18phr，固化条件RT／10h或80℃／3h。
贮存于阴凉、干燥的库房内，防潮。