1) low-molecular weight urethane polyisocyanate
低分子量氨基甲酸酯多异氰酸酯
2) PAPI
多苯基甲烷多异氰酸酯
1.
The lignin-based polyurethane(PU) films were prepared from wheat straw alkali lignin by solution casting with polyethylene glycol(PEG) 300 or 1 000 and polymeric phenyl methane-diisocyanate(PAPI) in the solvent of N,N-dimethylformamide(DMF).
以麦草碱木质素、相对分子质量为300和1 000的聚乙二醇(PEG)及多苯基甲烷多异氰酸酯(PAPI)为原料,以N,N-二甲基甲酰胺为溶剂,使用溶液浇注法固化成型工艺,制备了碱木质素聚氨酯薄膜。
2.
Lignin-based polyurethane(PU)films were prepared from wheat straw alkali lignin by solution casting with polyethylene glycol(PEG)and polymeric phenyl methane-diisocyanate(PAPI)in the solvent of N,N-dimethyl-formamide(DMF).
以麦草碱木质素、聚乙二醇(PEG)及多苯基甲烷多异氰酸酯(PAPI)为原料,以N,N-二甲基甲酰胺为溶剂,使用溶液固化成型法制备了碱木质素聚氨酯薄膜。
3) Polymethylene polyisocyanate
多亚甲基多异氰酸酯
4) Carbamic acid, cyano-, methyl ester
氰氨基甲酸甲酯
5) ethyl cyanocarbamate
氰氨基乙酸甲酯
6) methyl isothiocyanate
异硫氰酸甲基酯
1.
999 3), that was well matched with the regression of methyl isothiocyanate, y=0.
异硫氰酸丙基酯的标准曲线回归方程y=0 4182x+2 821(r2=0 9993)与异硫氰酸甲基酯的回归方程y=0 4122x+2 4423(r2=0 9966)基本拟合。
补充资料：低分子量氨基甲酸酯多异氰酸酯
分子式：
CAS号：
性质： 是由二异氰酸酯与低分子量二元醇或三元醇按异氰酸酯基:羟基(NCO:OH)≥2:1的比例加成制得带有游离异氰酸酯基的低分子量多异氰酸酯。常用的有甲苯二异氰酸酯(TDI)与三羟甲基丙烷的加成物和六亚甲基二异氰酸酯(HDI)或异佛尔酮二异氰酸酯(IPDI)与三羟甲基丙烷的加成物。该类异氰酸酯蒸气压低，光稳定性好，主要用于聚氨酯涂料或胶黏剂的固化剂。
CAS号：
性质： 是由二异氰酸酯与低分子量二元醇或三元醇按异氰酸酯基:羟基(NCO:OH)≥2:1的比例加成制得带有游离异氰酸酯基的低分子量多异氰酸酯。常用的有甲苯二异氰酸酯(TDI)与三羟甲基丙烷的加成物和六亚甲基二异氰酸酯(HDI)或异佛尔酮二异氰酸酯(IPDI)与三羟甲基丙烷的加成物。该类异氰酸酯蒸气压低，光稳定性好，主要用于聚氨酯涂料或胶黏剂的固化剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。