1) isostatic molding
等压成型
2) isostatic pressing
等静压成型
1.
They are discovered during the checkout process of the ceramic vacuum tubes produced by isostatic pressing method.
本文对等静压成型法生产的陶瓷真空管壳经常出现的废品进行了分类;结合生产实践,从原料、配方、成型、烧成、上釉等方面分析了废品产生的原因,提出了一些相应的改进措施。
2.
Adopting the isostatic pressing and hand-made to produce alumina ball respectively,the results shows that not only the ball's firing temperature and physical behavious,but also the wear regularity is influenced by the different forming methods.
分别采用等静压成型与手搓成型工艺制造氧化铝瓷球 ;研究表明不同的成型方法不仅对瓷球的烧成及物理性能有影响 ,且对其磨损规律有着很大的影响 ;等静压成型瓷球的烧结温度较手搓成型瓷球要低 ,硬度及密度比手搓成型瓷球要高 ;手搓成型瓷球的磨损率随时间增加而增加 ,等静压成型瓷球的磨损率随时间增加而相应减小。
3.
With high-purity A12O3,AlN and Al powders as raw materials and with Y2O3 and MgO as singtering additives,forming with cold isostatic pressing in 150 MPa,AlON transparent ceramics were obtained at 1850 ℃ for 1 h under nitrogen atmosphere.
本文采用高纯Al2O3、AlN和Al粉为原料,用Y2O3和MgO作为烧结助剂,在150MPa下等静压成型,然后在氮气氛下,1850℃保温1h制备出透明尖晶石型氮氧化铝(AlON)陶瓷。
3) isotactic mo(u)lding process
等压成型法
4) hot isostatic compaction
热等静压;热等压成型
5) cold isostatic pressing
冷等静压成型
1.
The advantages of green compacts formed by cold isostatic pressing (CIP) are high strength, high density, homogeneous density and so on.
冷等静压成型所得的坯体强度大、密度高而均匀,尤其具有实现坯体近、净尺寸成型等优点,利用反应烧结氮化硅陶瓷烧结前后尺寸不变的特点,使得氮化硅陶瓷可实现少加工或免加工,降低氮化硅陶瓷的生产成本。
2.
5)NbO_3 binary lead-free piezoceramic systems were prepared by the cold isostatic pressing and air-proof sintering techniques.
采用冷等静压成型和密闭烧结工艺,制备了具有微晶结构的稀土离子La~(3+)掺杂0。
6) HIP moulding
热等静压成型
补充资料：等压成型
分子式：
CAS号：
性质： 是聚四氟乙烯模压成型的一种，也称液压成型。它是利用高压流体的相同的压力向各处传递的帕斯卡定理，使橡胶袋胀大或缩小，将橡胶袋与成型模壁之间的聚四氟乙烯物料逐渐而均匀地压紧，使之成为所需形状的聚四氟乙烯预成型品。与普通模压成型相比，有设备简单、模具结构简单、操作方便、预成型品受压均匀、节约原料等优点，而普通模压成型难以加工成复杂异形制品和大、中型中空薄壁制品。