1) hot-isostatic-pressing(HIP)moulding technique
热等静压成型工艺
2) HIP and HP process
热等静压和热压工艺
3) hot isostatic compaction
热等静压;热等压成型
4) HIP moulding
热等静压成型
6) isostatic pressing
等静压成型
1.
They are discovered during the checkout process of the ceramic vacuum tubes produced by isostatic pressing method.
本文对等静压成型法生产的陶瓷真空管壳经常出现的废品进行了分类;结合生产实践,从原料、配方、成型、烧成、上釉等方面分析了废品产生的原因,提出了一些相应的改进措施。
2.
Adopting the isostatic pressing and hand-made to produce alumina ball respectively,the results shows that not only the ball's firing temperature and physical behavious,but also the wear regularity is influenced by the different forming methods.
分别采用等静压成型与手搓成型工艺制造氧化铝瓷球 ;研究表明不同的成型方法不仅对瓷球的烧成及物理性能有影响 ,且对其磨损规律有着很大的影响 ;等静压成型瓷球的烧结温度较手搓成型瓷球要低 ,硬度及密度比手搓成型瓷球要高 ;手搓成型瓷球的磨损率随时间增加而增加 ,等静压成型瓷球的磨损率随时间增加而相应减小。
3.
With high-purity A12O3,AlN and Al powders as raw materials and with Y2O3 and MgO as singtering additives,forming with cold isostatic pressing in 150 MPa,AlON transparent ceramics were obtained at 1850 ℃ for 1 h under nitrogen atmosphere.
本文采用高纯Al2O3、AlN和Al粉为原料,用Y2O3和MgO作为烧结助剂,在150MPa下等静压成型,然后在氮气氛下,1850℃保温1h制备出透明尖晶石型氮氧化铝(AlON)陶瓷。
补充资料：爆炸等静压成型
分子式：
CAS号：
性质：利用炸药的爆炸，产生高压冲击波传给液体介质，加压于模体，使粉料在各方向同时均匀受压。与一般等静压成型的区别在于：装置简单，不带附属的高压系统，爆炸的瞬间可达30000～100000MPa的巨大高压，操作周期短，成形后坯体密度高，硬度大，可再精加工。操作控制较难，要加强防护和安全。
CAS号：
性质：利用炸药的爆炸，产生高压冲击波传给液体介质，加压于模体，使粉料在各方向同时均匀受压。与一般等静压成型的区别在于：装置简单，不带附属的高压系统，爆炸的瞬间可达30000～100000MPa的巨大高压，操作周期短，成形后坯体密度高，硬度大，可再精加工。操作控制较难，要加强防护和安全。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。