1) phenolic-novolac epoxy based vinyl ester unsaturated polyester resin
酚醛环氧乙烯基酯不饱和聚酯树脂
2) novolac epoxy vinyl ester resin
酚醛环氧乙烯基酯树脂
3) epoxy novalac type vinyl ester resin
环氧酚醛乙烯基酯树脂
4) vinyl ester based unsaturated polyester resin
乙烯基酯不饱和聚酯树脂
1.
The processing of glass-reinforced plastic cover for Model 16 Hooker electrolyzer with vinyl ester based unsaturated polyester resin was introduced.
叙述了用乙烯基酯不饱和聚酯树脂制作虎克－１６型玻璃钢电解槽盖的施工方法，介绍了乙烯基酯不饱和聚酯树脂的性能。
5) NEVER
[英]['nevə(r)] [美]['nɛvɚ]
酚醛环氧型乙烯基酯树脂
1.
The swelling properties of epoxy vinyl ester resin(NEVER)/2-hydroxyethyl methacrylate(HEMA) copolymeric hydrogels were investigated.
该文研究了酚醛环氧型乙烯基酯树脂(NEVER)/甲基丙烯酸-β-羟乙酯(HEMA)共聚水凝胶的溶胀性质。
6) bisphenol-A epoxide vinylester resin
双酚A环氧乙烯基酯树脂
1.
Resin transfer molding(RTM) mould was manufactured with bisphenol-A epoxide vinylester resin as matrix,poly(vinyl acetate) as low shrinkage additive and glass fiber tricot as reinforcing material,according to the basic requirement of matrix resin of RTM mould.
根据树脂传递模塑(RTM)模具对基体树脂的基本要求,选用双酚A环氧乙烯基酯树脂为基体,聚乙酸乙烯酯为低收缩添加剂,玻璃纤维经编织物为增强材料,并加入相应的助剂,制备了复合材料RTM模具。
补充资料：酚醛环氧乙烯基酯不饱和聚酯树脂
分子式：
CAS号：
性质：含有酚醛环氧甲基丙烯酸酯结构的不饱和聚酯树脂。较双酚A二缩水甘油醚(即双酚A环氧)型乙烯基酯聚酯交联密度大、热变形温度高、耐热性好，但可挠性和耐碱性稍差。多数性能基本相似。铸塑料热变形温度129℃。增强塑料的拉伸强度29.42MPa，拉伸模量17.16GPa，弯曲强度31.36MPa，弯曲模量14.7GPa，冲击强度86kJ/m2；体积电阻率5.41×1013Ω·cm，介电强度25.9MV/m。由苯酚、甲醛制成线型酚醛树脂后，再与甲基丙烯酸反应制得。可制作玻璃纤维增强塑料和铸塑料等用于耐高温、耐腐蚀和耐溶剂等方面的设备和零部件。
CAS号：
性质：含有酚醛环氧甲基丙烯酸酯结构的不饱和聚酯树脂。较双酚A二缩水甘油醚(即双酚A环氧)型乙烯基酯聚酯交联密度大、热变形温度高、耐热性好，但可挠性和耐碱性稍差。多数性能基本相似。铸塑料热变形温度129℃。增强塑料的拉伸强度29.42MPa，拉伸模量17.16GPa，弯曲强度31.36MPa，弯曲模量14.7GPa，冲击强度86kJ/m2；体积电阻率5.41×1013Ω·cm，介电强度25.9MV/m。由苯酚、甲醛制成线型酚醛树脂后，再与甲基丙烯酸反应制得。可制作玻璃纤维增强塑料和铸塑料等用于耐高温、耐腐蚀和耐溶剂等方面的设备和零部件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。