1) epoxy vinyl ester resin
环氧乙烯基酯树脂
1.
All kinds of structure factors causing the stability of epoxy vinyl ester resin in acid,alkali or salt solutions were particularly discussed in this paper.
较为详细论述了影响环氧乙烯基酯树脂在酸、碱、盐溶液中稳定性的各种结构因素。
2.
In this lecture,the stability of epoxy vinyl ester resins in organic solvents was related and the solubility parameters of three epoxy vinyl ester resins were determined by experiment.
对环氧乙烯基酯树脂在有机溶剂中的稳定性作了理论上的探讨,并提供了3种环氧乙烯基酯树脂的溶解度参数实验数据。
3.
MFE-VARIM-200 epoxy vinyl ester resin for wind turbine blade was developed.
简述了国内外风力发电发展概况及风机叶片成型工艺及要求,研制了风力发电机叶片用MFE-VARIM-200环氧乙烯基酯树脂,对该树脂的粘度、凝胶时间、固化收缩率及固化物的力学性能等进行了测试。
2) vinyl ester resin
环氧乙烯基酯树脂
1.
A bisphenol-F-epoxy resin (EP) toughening was performed by incorporating bisphenol-A-vinyl ester resin (VER) and cured simultaneously with it to form an interpenetrating polymer network (IPN).
使用双酚A型环氧乙烯基酯树脂(VER)与双酚F型环氧树脂(EP)同步固化的方法对环氧树脂进行增韧改性。
2.
This article analyses the corrosion mechanism of carbamide product terrace, presents some features of vinyl ester resin and polyurea elastomer material,comprehensive appraise the anticorrosive effect of two material on carbamide platform.
对尿素成品地坪腐蚀机理进行了分析 ,介绍了环氧乙烯基酯树脂、聚脲弹性体的性能特点 ,综合评价两种防腐材料应用于尿素地坪防腐的效果。
3.
The relation of molecular structure to physicalmechanical properties of epoxy vinyl ester resin and the correlation between different kinds of physicalmechanical properties,such as distortion temperature,tensile strength,tensile modulus and elongation at break,were discussed in this paper.
论述了环氧乙烯基酯树脂的物理、力学性能与分子结构之间的依赖关系以及各性能间的相互关系。
3) bisphenol-A epoxide vinylester resin
双酚A环氧乙烯基酯树脂
1.
Resin transfer molding(RTM) mould was manufactured with bisphenol-A epoxide vinylester resin as matrix,poly(vinyl acetate) as low shrinkage additive and glass fiber tricot as reinforcing material,according to the basic requirement of matrix resin of RTM mould.
根据树脂传递模塑(RTM)模具对基体树脂的基本要求,选用双酚A环氧乙烯基酯树脂为基体,聚乙酸乙烯酯为低收缩添加剂,玻璃纤维经编织物为增强材料,并加入相应的助剂,制备了复合材料RTM模具。
4) novolac epoxy vinyl ester resin
酚醛环氧乙烯基酯树脂
5) epoxy novalac type vinyl ester resin
环氧酚醛乙烯基酯树脂
6) epoxy vingl ester resin
环氧乙烯基树脂
补充资料：酚醛环氧乙烯基酯不饱和聚酯树脂
分子式：
CAS号：
性质：含有酚醛环氧甲基丙烯酸酯结构的不饱和聚酯树脂。较双酚A二缩水甘油醚(即双酚A环氧)型乙烯基酯聚酯交联密度大、热变形温度高、耐热性好，但可挠性和耐碱性稍差。多数性能基本相似。铸塑料热变形温度129℃。增强塑料的拉伸强度29.42MPa，拉伸模量17.16GPa，弯曲强度31.36MPa，弯曲模量14.7GPa，冲击强度86kJ/m2；体积电阻率5.41×1013Ω·cm，介电强度25.9MV/m。由苯酚、甲醛制成线型酚醛树脂后，再与甲基丙烯酸反应制得。可制作玻璃纤维增强塑料和铸塑料等用于耐高温、耐腐蚀和耐溶剂等方面的设备和零部件。
CAS号：
性质：含有酚醛环氧甲基丙烯酸酯结构的不饱和聚酯树脂。较双酚A二缩水甘油醚(即双酚A环氧)型乙烯基酯聚酯交联密度大、热变形温度高、耐热性好，但可挠性和耐碱性稍差。多数性能基本相似。铸塑料热变形温度129℃。增强塑料的拉伸强度29.42MPa，拉伸模量17.16GPa，弯曲强度31.36MPa，弯曲模量14.7GPa，冲击强度86kJ/m2；体积电阻率5.41×1013Ω·cm，介电强度25.9MV/m。由苯酚、甲醛制成线型酚醛树脂后，再与甲基丙烯酸反应制得。可制作玻璃纤维增强塑料和铸塑料等用于耐高温、耐腐蚀和耐溶剂等方面的设备和零部件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。