1) alumina zirconia carbon brick
铝锆碳砖
2) Cr_2O_3-ZrO_2-Al_2O_3 bricks
铬锆铝砖
1.
Corrosion of Cr_2O_3-ZrO_2 -Al_2O_3 bricks used in water-coal gasifier;
利用扫描电镜及能谱仪对水煤浆气化炉用进口铬锆铝砖的蚀变过程进行了显微观察与分析。
3) Cr_2O_3-Al_2O_3ZrO_2 brick
铬铝锆砖
4) zircon-alumina brick
锆铝砖
5) zirconia-carbon brick
锆碳砖
6) Al2O3-ZrO2-C
铝锆碳
1.
21 μm)and contents of silicon powder(1%,3%,5%,7%)on cold crushing strength(CCS),pore size distribution and microstructure of Al2O3-ZrO2-C refractories coked at high temperature were investigated by mercury porosimeter,scanning electron microscope(SEM),and energy dispersive spectrometer(EDS),etc.
21μm)依次变小)和含量(分别为1%、3%、5%、7%)对埋炭烧成铝锆碳材料的耐压强度、孔径分布和显微结构的影响。
2.
The effects of the sintering temperature and the content of graphite on the properties of Al2O3-ZrO2-C materials are studied experimentally.
为提高铝锆碳耐火材料的性能,研究了烧成温度对铝锆碳耐火材料气孔率、体积密度、常温耐压强度的影响,得出了适宜的烧成温度范围和最佳的锆莫来石加入量,并对此进行了理论分析。
3.
The clogging mechanism of Al2O3-ZrO2-C based submerged nozzle was investigated in the light of clogging condition of submerged nozzle in the process of joint casting.
针对连铸过程浸入式水口的堵塞情况,研究了铝锆碳复合浸入式水口堵塞的形成机理。
补充资料：铝锆碳砖
分子式：
CAS号：
性质：一种氧化铝、氧化锆系耐火材料，含氧化铝64％～72％，氧化锆6％～9％，碳加碳化硅8.5％～15％。加入氧化锆大大提高了材料的抗热震性、耐蚀性、导热性和对熔融金属及渣的不湿润性。体积密度3.0g/cm2，耐压强度110MPa，显孔率6％～12％。采用机压或等静压成型，经高温烧成。用作盛钢桶整体塞棒砖、滑动水口滑板砖等。
CAS号：
性质：一种氧化铝、氧化锆系耐火材料，含氧化铝64％～72％，氧化锆6％～9％，碳加碳化硅8.5％～15％。加入氧化锆大大提高了材料的抗热震性、耐蚀性、导热性和对熔融金属及渣的不湿润性。体积密度3.0g/cm2，耐压强度110MPa，显孔率6％～12％。采用机压或等静压成型，经高温烧成。用作盛钢桶整体塞棒砖、滑动水口滑板砖等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。