1) calcium hexa-aluminate
六铝酸一钙
2) calcium hexaluminate
六铝酸钙
1.
The large amount of microporosity in calcium hexaluminate insulating refractory keeps its thermal conductivity at low levels from room temperature to 1 500 ℃,which makes calcium hexaluminate insulating refractory as a unique novel insulating material.
六铝酸钙(CA6)隔热耐火材料有着大量的微米级气孔,故其热导率从室温至1500℃均保持在较低水平,这使其成为一种独特的新型隔热耐火材料。
2.
Calcium hexaluminate (CA 6) was synthesized by reaction sintering of two kinds of mixtures of CaCO 3/α-Al 2O 3 and pure calcium aluminate cement/α-Al 2O 3,respectively.
分别采用轻质碳酸钙和活性氧化铝 ,或纯铝酸钙水泥和活性氧化铝为初始原料 ,反应烧结合成了六铝酸钙 (CA6)材料 ,研究了原料和成型压力对合成材料的烧结性能和显微结构的影响 ,同时借助于XRD、TG -DSC、SEM和EDAX等测试手段对其反应过程、物相变化和显微结构进行了分析和观察。
3.
Calcium dialuminate (CA2) and Calcium hexaluminate (CA6) occur at CaO-Al2O3 system as important compounds.
二铝酸钙(CA_2)和六铝酸钙(CA_6)是CaO-Al_2O_3二元体系中两类重要化合物。
3) monocalcium aluminate
铝酸一钙
4) calcimn dialuminate
二铝酸一钙
5) hexagonal calcium aluminate hydrate
六方水合铝酸钙
1.
The nanometer hexagonal calcium aluminate hydrate(C4AHx) particles were prepared by liquid phase sedimentation.
采用液相沉淀法制备了纳米六方水合铝酸钙(C4AHx),在单因素实验的基础上,通过正交实验确定了合成纳米六方水合铝酸钙的最佳工艺条件。
2.
Synthesis condition and method of hexagonal calcium aluminate hydrate are described.
叙述了六方水合铝酸钙的合成条件和方法 ,并通过化学分析、TG -DTA分析和XRD分析对所合成的六方水合铝酸钙进行了表征。
6) monocalcium aluminate hydrate
水化铝酸一钙
补充资料：六铝酸一钙
分子式： CaO·6Al2O3
CAS号：
性质：白色固体。密度3.54～3.9g/cm3。当与少量硅、钛、铁氧化物形成固溶体时，颜色变蓝或绿色。约1830℃不一致熔融为氧化铝和液相。通过高温固相反应生成。存在于低钙铝酸盐水泥熟料中，为惰性矿物，无水硬性。
CAS号：
性质：白色固体。密度3.54～3.9g/cm3。当与少量硅、钛、铁氧化物形成固溶体时，颜色变蓝或绿色。约1830℃不一致熔融为氧化铝和液相。通过高温固相反应生成。存在于低钙铝酸盐水泥熟料中，为惰性矿物，无水硬性。