1) 4-calcium 2-aluminium sulfide 10-oxide 12-hydrate
一元型含水硫铝酸钙
2) 6-calcium 2-aluminium sulfide 18-oxide 6-hydrate
三元型含水硫铝酸钙
1.
Study of thermodynamics of 4-calcium 2-aluminium sulfide 10-oxide 12-hydrate and 6-calcium 2-aluminium sulfide 18-oxide 6-hydrate;
一元和三元型含水硫铝酸钙热力学研究
3) 3CaO·Al 2O 3·CaSO 4·12H 2O
含水硫铝酸钙
5) Ba_bearing calcium sulphoaluminate
含钡硫铝酸钙
1.
Based on C 4A 3S(3CaO·3Al 2O 3·CaSO 4) which is the main mineral in sulphoaluminate cement, the Ba_bearing calcium sulphoaluminate series of new cement mineral are synthesized by substitution of analytical pure chemical reagent BaCO 3, BaSO 4 for Ca ions.
以硫铝酸盐水泥的主要矿物Ｃ４Ａ３Ｓ（３ＣａＯ·３Ａｌ２Ｏ３·ＣａＳＯ４）为基础，用分析纯化学试剂ＢａＣＯ３ ，ＢａＳＯ４ 对Ｃ４Ａ３Ｓ中的Ｃａ 离子进行取代，合成了一种新水泥矿物———含钡硫铝酸钙系列矿物，并研究了该系列矿物的强度发展规律。
6) calcium sulphoaluminate
无水硫铝酸钙
1.
Under the process conditions,qualified sulphoaluminate cement clinker can be produced and main mineral composition of cement clinker are calcium sulphoaluminate and dicalcium silicate.
结果表明:用本试验所采用的原料,配料比为m(矾土)∶m(石灰石)∶m(脱硫石膏)=35∶43∶22,煅烧温度为1400℃可烧制成矿物组成为无水硫铝酸钙和硅酸二钙的合格硫铝酸盐水泥熟料。
补充资料：硫铝酸钙
分子式：3CaO·3Al2O3·Ca-SO4
CAS号：
性质：等轴晶系。密度2.61g/cm3。折射率nD1.568。1400℃以上可分解为铝酸钙、氧化钙和三氧化硫。可由氧化钙、三氧化二铝和硫酸钙于1000～1250℃反应生成。是一种早强矿物，是快硬、膨胀、自应力水泥的主要组成。也可作为硅酸盐水泥的早强剂、速凝剂和膨胀剂。
CAS号：
性质：等轴晶系。密度2.61g/cm3。折射率nD1.568。1400℃以上可分解为铝酸钙、氧化钙和三氧化硫。可由氧化钙、三氧化二铝和硫酸钙于1000～1250℃反应生成。是一种早强矿物，是快硬、膨胀、自应力水泥的主要组成。也可作为硅酸盐水泥的早强剂、速凝剂和膨胀剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。