1)  moulding by centrifugal casting
离心注浆成型
2)  Centricfugal-Casting
离心注浆
3)  Casting-centrifugate
浇注离心成型
4)  slip casting
注浆成型
1.
Anode supported SOFCs prepared by slip casting technique and its performance;
注浆成型制备阳极支撑型SOFC及其性能
2.
Cone-shaped cylindrical anode supported SOFCs by slip casting formation method;
注浆成型法制备阳极支撑锥管状SOFC
3.
Crucible samples are formed by slip casting with that materials.
以注浆成型法制备感应炉坩埚,考察所制得样品的理化性能。
5)  centrifugal infiltrate casting
离心渗透注浆法
1.
Objective To investigate the mechanical properties and microstructure of nano-zirconia toughened alumina ceramics with variety of nano-zirconia content in centrifugal infiltrate casting processing of dental all-ceramic.
方法将纳米氧化锆、氧化铝、复合添加剂等粉料与一定比例的醇—水混合后,球磨制备浆液,采用离心渗透注浆法成坯,在1450℃下烧结8h。
6)  centrifugal casting
离心成型
1.
A suspension with good rheology and suitable for centrifugal casting was prepared from two Al2O3 powders with different particle sizes by choosing the appropriate process.
选用两种粒径大小不同的氧化铝粉体,通过选择分散工艺配制了适合离心成型的流变性好的浆料。
2.
Concerning the slurry for centrifugal casting of high\|density and high\|strength Al 2O 3 ceramics, the paper discusses the effect of its dispersent agent, pH value and solid content of the viscosity of the slurry.
针对高密度、高强度99Al2O3陶瓷离心成型用悬浮浆料,研讨了分散剂、pH 值、固相含量等因素对悬浮浆料粘度的影响。
3.
With a slurry of Al2O3 powders and N-Methyloacrylamide-based polymerization system,pore-gradient alumina tubes of diameters 12,18 and 30 mm were fabricated in one pot by centrifugal casting combined with gelcasting method.
选用Al2O3粉体和单体为N-羟甲基丙烯酰胺(NMA)的聚合体系配成浆料,结合凝胶注模和离心成型工艺的优点,制备出直径分别为12、18、30 mm的具有一次成型孔梯度结构的管式Al2O3陶瓷坯体。
补充资料:离心注浆成型
分子式:
CAS号:

性质:利用模型不停旋转产生的离心力以加速坯体形成的注浆成型方法。坯体组织比较致密,颗粒排列比较均匀,可减少由注浆过程产生的制品缺陷。 

说明:补充资料仅用于学习参考,请勿用于其它任何用途。