1)  Oxirane, (butoxymethyl)-
环氧丙烷丁基醚660型
2)  Glycidyl butyl ethrel
环氧丙烷丁基醚660型
3)  Epoxypropane butyl ether
环氧丙烷丁基醚660型
4)  epoxy resin
环氧
1.
Effect of Polyether on Preparation of Epoxy Resin-PU IPN;
聚醚对环氧-聚氨酯互穿网络制备的影响
2.
The title oil resistant coatings for fuel tanks has been developed by choosing proper polyester resin,epoxy resin and appropriate polyisocanate hardener,The results indicated that the coatings shows good low temperature drying property and corrosion protection, oil-resistance,particularly hot-oil-resistance.
通过选择适当的聚酯树脂和环氧树脂,配以适当的异氰酸固化剂,研制了一种用于油箱的环氧聚氨酯耐油涂料。
3.
In this paper, the application and development of epoxy resins act as the inhibitor of rocket propellant are reviewed; the recent progress of work is also introduced.
综述了环氧包覆材料的历史发展和国内外现状 ,根据环氧树脂增韧改性的进展 ,提出了环氧包覆材料的发展方向。
5)  epoxy
环氧
1.
Research development of waterborne curing agent for epoxy resin;
水性环氧固化剂的研究进展
2.
The self assembly at carbon fiber/epoxy interface in composites;
碳纤维增强环氧复合材料的界面自组装
3.
Preparation and optical properties of ZnO/epoxy nanocomposites;
氧化锌/环氧纳米复合材料的制备及其光学性能研究
6)  oxido-
（环）氧
参考词条
补充资料：环氧丙烷丁基醚660型
分子式：C7H14O2
分子量：130.19
CAS号：2426-08-6

性质：无色透明液体。相对密度0.915，沸点164℃，折光率1.420，闪点59℃。可溶于丙酮、苯、醇，不溶或难溶于水。

制备方法：由丁醇和环氧氯丙烷为原料，经两步反应合成。具体工艺过程为：将267kg丁醇和32kg浓度为96%的浓硫酸加入反应釜，搅拌，升温至55℃，滴加环氧氯丙烷324kg，温度控制在55-60℃约4h加完，再在60-65℃保温2h。然后，冷却至45℃，缓缓加入四氯化锡与丁醇的混合液（5kg四氯化锡溶于5kg丁醇中），再在60-65℃保温反应4h，反应完后，减压蒸馏回收未反应的环氧氯丙烷和丁醇，直至温度达到85-95℃，真空度93.1kPa下无环氧氯丙烷和丁醇蒸出为止。得到表氯醇丁基醚。将上述反应物料冷至30-35℃，滴加浓度30%的氢氧化钠432kg，约4h加完，然后升温至35-40℃并保温反应3h，再在搅拌下加入纯苯，升温至放掉盐水和碱水，然后水洗使pH约为6.5-7。放掉洗涤水，升温常压脱苯，直至料液温度达至140℃，然后冷却放料。两步总收率以丁醇计约为95%。

用途：该品可作双酚A环氧树脂的活性稀释剂。毒性小，使用方便。并能改善一些树脂硬化后的性能，如抗冲强度等。

说明：补充资料仅用于学习参考，请勿用于其它任何用途。