1)  PAPI
多苯基多亚甲基多异氰酸酯
2)  PAPI
多亚甲基多苯基多异氰酸酯
1.
Influence of acrylic acid content,initiator content,and PAPI content on emulsion shear strength are studied,and the relation between initiator content,temperature-maintaining time and emulsion conversion are also investigated.
研究了丙烯酸用量、引发剂用量和多亚甲基多苯基多异氰酸酯用量对乳液剪切强度的影响,同时还研究了引发剂用量和保温时间与乳液转化率的关系。
2.
In order to get a kind of adhesive for hemlock (Tsuga Dumosa) splice with excellent properties, based on the N-Hydroxymethyl acrylamide (NMA) modified polyvinyl acetate (PVAC) emulsion, using polyarylpolymethylene -isocyanate (PAPI) as crosslink agent,the properties of adhesive for hemlock splice were discussed in this paper.
为得到一种性能优异的铁杉拼板胶,以多亚甲基多苯基多异氰酸酯(PAPI)为交联剂,对N-羟甲基丙烯酰胺(NMA)改性聚醋酸乙烯酯(PVAc)乳液胶的性能进行测试。
3.
The research results showed that the effect of PAPI content was most prominent on bonding performance at the normal temperature,the stress time was secondly,the effects of starch content and stress were non obvious on bonding performance.
采用正交实验法,研究了以醋酸乙烯酯(VAc)共聚乳液为主剂、多亚甲基多苯基多异氰酸酯(PAPI)为交联剂的双组分木材胶粘剂的胶接工艺与性能。
更多例句>>
3)  polyisocyanate(PAPI)
多亚甲基多苯基多异氰酸酯(PAPI)
4)  Polymethylene polyisocyanate
多亚甲基多异氰酸酯
5)  polymethylene polyphenyl isocyanate
多亚甲基多苯基异氰酸酯
例句>>
6)  PAPI
多苯基甲烷多异氰酸酯
1.
The lignin-based polyurethane(PU) films were prepared from wheat straw alkali lignin by solution casting with polyethylene glycol(PEG) 300 or 1 000 and polymeric phenyl methane-diisocyanate(PAPI) in the solvent of N,N-dimethylformamide(DMF).
以麦草碱木质素、相对分子质量为300和1 000的聚乙二醇(PEG)及多苯基甲烷多异氰酸酯(PAPI)为原料,以N,N-二甲基甲酰胺为溶剂,使用溶液浇注法固化成型工艺,制备了碱木质素聚氨酯薄膜。
2.
Lignin-based polyurethane(PU)films were prepared from wheat straw alkali lignin by solution casting with polyethylene glycol(PEG)and polymeric phenyl methane-diisocyanate(PAPI)in the solvent of N,N-dimethyl-formamide(DMF).
以麦草碱木质素、聚乙二醇(PEG)及多苯基甲烷多异氰酸酯(PAPI)为原料,以N,N-二甲基甲酰胺为溶剂,使用溶液固化成型法制备了碱木质素聚氨酯薄膜。
补充资料：多苯基多亚甲基多异氰酸酯
    多苯基多亚甲基多异氰酸酯，简称PAPI，或称粗MDI，浅黄色至褐色粘稠液体．有刺激性气味。相对密度(20℃／20 ℃)1．2，燃点218℃。PAPI实际上是由50％MDI与50％官能度大于2以上的多异氰酸酯组成的混合物。升温时能发生自聚作用。溶于氯苯、邻二氯苯、甲苯等。PAPI的活性低，蒸气压低，只是TDI的百分之一，故毒性很低。
    用于制造聚氨脂胶粘剂。也可直接加入橡胶胶粘剂中，改善橡胶与尼龙或聚酯线的粘接性能。贮存于阴凉、通风、干燥的库房内，远离火种、热源。严格防水、防潮，避免光照。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。