1) tetraethoxysilane(TEOS)
硅酸乙酯(TEOS)
2) tetraethylorthosilicate (TEOS)
正硅酸乙酯(TEOS)
3) Tetraethyloxysilane (TEOS)
四乙氧基硅烷(TEOS)
4) Ethyl Silicate
硅酸乙酯
1.
TiO 2 photocatalytic coating was then prepared on a slide substrate, with ethyl silicate as the binder.
采用溶胶-凝胶法制得了添加La2O3 的改性TiO2 微粉,用硅酸乙酯作粘结剂,将TiO2 光催化涂层涂覆在载玻片上,讨论了TiO2 含量(质量分数,下同)以及活性炭和沸石对涂层光催化活性的影响。
2.
This paper reviews several industrial processes of ethyl silicate, and presents new semi-continuous process.
综述了硅酸乙酯几种工业生产工艺,对其特点进行了评述,并介绍了作者开发的半连续化生产新工艺。
3.
The hydrolizaion process of ethyl silicate in absence of ethanol is described.
硅酸乙酯的无酵水解工艺及各种因素对水解液性能的影响，指出这种工艺所获得的强度比传统的有醇水解工艺高，并可降低成本。
5) ethyl orthosilicate
硅酸乙酯
1.
When tetraethyl orthosilicate instead of tetrabutyl titanate, the gelation time can be much longer.
若以常用的硅酸乙酯代替钛酸丁酯，则胶凝时间明显延长，最终产物为β和α氧化铁的混晶相（γ－Ｆｅ２Ｏ３为主晶相），晶粒尺寸约为１０ｎｍ，并从中提出了一条改进γ－Ｆｅ２Ｏ３基气敏材料性能的新思路。
6) TEOS
硅酸乙酯
1.
The sol-gel coating was prepared with cellulosic fabrics and synthetic fabrics as carriers and TEOS as precursor.
以纤维素织物和合成纤维织物为载体,以硅酸乙酯(TEOS)为水解前驱体,对织物载体进行溶胶凝胶涂层整理。
2.
Silica sol without ethanol was prepared with tetraethyl orthosilicate(TEOS) as precursor.
以硅酸乙酯(TEOS)为水解前驱体,制备了有机硅水溶胶体系。
补充资料：硅酸乙酯
分子式 (C2H50)4Si
性质 无色易燃液体，有刺激性气味，相对密度0.9356(20/20℃)。沸点168.1℃。熔点110℃（升华）。蒸气压（20℃）133.322Pa。闪点（开杯）51.67℃。凝固点-77℃。粘度（20℃）17.9mPa·s，不溶于水，溶于乙醇，微溶于苯。水解生成二氧化硅的胶粘物。
用途 主要用作光学玻璃、耐化学品涂料及耐热涂料和粘合剂
毒性 本品低毒，对呼吸道和眼睛有较强的刺激作用。空气中最高容许浓度850mg/m3。生产现场防止粉尘飞扬，操作人员应穿戴防护用具。
包装储运 用玻璃瓶密封包装，外用木箱加固。存放于危险品仓库中，按铁路危规84064号规定运输。
性质 无色易燃液体，有刺激性气味，相对密度0.9356(20/20℃)。沸点168.1℃。熔点110℃（升华）。蒸气压（20℃）133.322Pa。闪点（开杯）51.67℃。凝固点-77℃。粘度（20℃）17.9mPa·s，不溶于水，溶于乙醇，微溶于苯。水解生成二氧化硅的胶粘物。
用途 主要用作光学玻璃、耐化学品涂料及耐热涂料和粘合剂
毒性 本品低毒，对呼吸道和眼睛有较强的刺激作用。空气中最高容许浓度850mg/m3。生产现场防止粉尘飞扬，操作人员应穿戴防护用具。
包装储运 用玻璃瓶密封包装，外用木箱加固。存放于危险品仓库中，按铁路危规84064号规定运输。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。