1) Cu-containing TEOS
含铜硅酸乙酯
2) Co-containing tetraethyl orthosilicate
含钴硅酸乙酯
1.
In this paper, Co-rich Co/SiO 2 composite aerogels in which mass fraction of Co can reach 66% were firstly prepared by sol-gel process of Co-containing tetraethyl orthosilicate (Co-TEOS).
本工作首次采用含钴硅酸乙酯 (Co_TEOS)进行溶胶 -凝胶反应来制备高钴含量的纳米级Co/SiO2 复合气凝胶 ,制备的Co/SiO2 复合气凝胶中n(Co)∶n(Si)的比例最高可达 2∶1,且复合气凝胶中的Co含量可在小于 6 6 % (质量分数 )的范围内任意调节 ,并系统研究了水量、催化剂浓度、溶剂量及含钴硅酸乙酯的组成对溶胶 -凝胶过程的影响 。
3) Ethyl Silicate
硅酸乙酯
1.
TiO 2 photocatalytic coating was then prepared on a slide substrate, with ethyl silicate as the binder.
采用溶胶-凝胶法制得了添加La2O3 的改性TiO2 微粉,用硅酸乙酯作粘结剂,将TiO2 光催化涂层涂覆在载玻片上,讨论了TiO2 含量(质量分数,下同)以及活性炭和沸石对涂层光催化活性的影响。
2.
This paper reviews several industrial processes of ethyl silicate, and presents new semi-continuous process.
综述了硅酸乙酯几种工业生产工艺,对其特点进行了评述,并介绍了作者开发的半连续化生产新工艺。
3.
The hydrolizaion process of ethyl silicate in absence of ethanol is described.
硅酸乙酯的无酵水解工艺及各种因素对水解液性能的影响，指出这种工艺所获得的强度比传统的有醇水解工艺高，并可降低成本。
4) ethyl orthosilicate
硅酸乙酯
1.
When tetraethyl orthosilicate instead of tetrabutyl titanate, the gelation time can be much longer.
若以常用的硅酸乙酯代替钛酸丁酯，则胶凝时间明显延长，最终产物为β和α氧化铁的混晶相（γ－Ｆｅ２Ｏ３为主晶相），晶粒尺寸约为１０ｎｍ，并从中提出了一条改进γ－Ｆｅ２Ｏ３基气敏材料性能的新思路。
5) TEOS
硅酸乙酯
1.
The sol-gel coating was prepared with cellulosic fabrics and synthetic fabrics as carriers and TEOS as precursor.
以纤维素织物和合成纤维织物为载体,以硅酸乙酯(TEOS)为水解前驱体,对织物载体进行溶胶凝胶涂层整理。
2.
Silica sol without ethanol was prepared with tetraethyl orthosilicate(TEOS) as precursor.
以硅酸乙酯(TEOS)为水解前驱体,制备了有机硅水溶胶体系。
补充资料：原硅酸乙酯
分子式：C8H20O4SI
分子量：208.33
CAS号：
密度：0.9320
熔点：-82.5℃
沸点：168.8℃
闪点：51.67℃
粘度：17.9
折射率：1.3928
性状：无色或淡棕色液体，略有香味。
用途：用于制造耐化学品涂料和耐热涂料。也用于制备有机硅的溶剂。
制备或来源：由四氯化硅和无水乙醇作用后经蒸馏而得。
分子量：208.33
CAS号：
密度：0.9320
熔点：-82.5℃
沸点：168.8℃
闪点：51.67℃
粘度：17.9
折射率：1.3928
性状：无色或淡棕色液体，略有香味。
用途：用于制造耐化学品涂料和耐热涂料。也用于制备有机硅的溶剂。
制备或来源：由四氯化硅和无水乙醇作用后经蒸馏而得。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。