1) Burn-in socket
预烧承座
2) core frame for burning
承烧座
1.
So far the high grade mullite-corundum core frame for burning materials for deflection magnetic core have not been developed because the research on this subject state late in China.
由于我国对偏转磁芯承烧座的研制较晚，至今没有研制出高档的莫来石—刚玉质承烧座。
4) calcination
[英][,kælsi'neiʃən] [美][,kælsɪ'neʃən]
预烧
1.
The effects of calcination and sintering technique on the dielectric properties of (Zr08Sn02)TiO4 system ceramics were investigated.
研究了预烧和烧结工艺对(Zr0。
2.
Without calcination of TiO2 and BaCO3, a mixture of pre-reaction powders (PbO+ZnNb2O6) and TiO2 and BaCO3 was pressed and sintered directly.
采用改进的工艺路线制备了化学计量比的Pb(Zn1／3Nb2/3)O3-PbTiO3-BaTiO3陶瓷,二氧化钛和碳酸钡不经过预烧,与预反应粉体混合球磨,成型后直接烧结,在1100℃和1120℃分别保温1 h,2 h,4 h获得了100％钙钛矿结构的PZN-PT-BT陶瓷,最大密度7。
5) preheat
[英][,pri:'hi:t] [美][pri'hit]
预烧
1.
Ti-Mn-Cu substituted barium ferrite have been prepared in condition of different preheat temperature by coprecipitationt method.
本文用共沉淀法,在不同的预烧温度下合成了Ti、Mn、Cu掺杂的M-型钡铁氧体,考察了在不同预烧条件下,铁氧体的形成情况,以及离子的掺杂对铁氧体的磁性能的影响。
6) Presintering
预烧
1.
The process conditions,including presintering temperature,sintering temperature and time,cooling mode and pretreatment were studied.
对烧成过程(预烧温度、烧结温度及保温时间、降温方式)及预处理工艺进行了研究。
2.
The influence of presintering powder,Mg content and sintering temperature on microstructure of target is studied by scanning electron microscopy(SEM) and X-ray diffraction(XRD).
以纳米级的ZnO、MgO和Al2O3粉体为原料,经过湿式球磨得到了混合粉体,采用常压固相烧结的方法制备了高致密度MgxZn1-xO:Al陶瓷靶材,研究了预烧粉体、Mg掺杂量和烧结温度对靶材微观结构和性能的影响。
补充资料：预烧
分子式：
CAS号：
性质：在制成耐火制品前，预先对原料进行热处理的工艺。原料在预烧时将产生一系列的物理化学反应，作为坯料能改善制品的成分及其组织结构，保证制品的体积稳定及其外形尺寸的准确性，提高制品的性能。预烧依材质和使用要求而异，可以分为活化烧结、轻烧、死烧和二步煅烧等。
CAS号：
性质：在制成耐火制品前，预先对原料进行热处理的工艺。原料在预烧时将产生一系列的物理化学反应，作为坯料能改善制品的成分及其组织结构，保证制品的体积稳定及其外形尺寸的准确性，提高制品的性能。预烧依材质和使用要求而异，可以分为活化烧结、轻烧、死烧和二步煅烧等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条