2) Al-Zn-Mg-Cu-Zr
Al-Zn Mg-Cu-Zr
4) Al-Zn-Mg-Cu aluminum alloy
Al-Zn-Mg-Cu系铝合金
1.
Al-Zn-Mg-Cu aluminum alloy under anealing state was extruded at the temperature of 523 K through various pass equal channel angular pressing (ECAP) technique, and the real strain is up to 6.
通过对退火态的Al-Zn-Mg-Cu系铝合金在523K加热进行不同道次等径通道挤压(ECAP),采用120°模具在Bc路径下经10次ECAP变形后等效真应变达到6。
5) Al-Zn-Mg-Cu-Sc-Zr hexbasic system
Al-Zn-Mg-Cu-Sc-Zr六元系
1.
The current status of study of Al-Zn-Mg-Cu-Sc-Zr hexbasic system in the aluminum-rich region in recent years is reviewed.
总结了近年来Al-Zn-Mg-Cu-Sc-Zr六元系相图的发展情况,分析了Al-Zn-Mg-Cu-Sc-Zr六元系中富铝角存在的中间相Al3Sc、Al3Zr、Al3(Sc1-xZrx)、W相(ScCu6。
6) Al-Zn-Cu system
Al-Zn-Cu系
1.
It was affirmed that the stable Al+Zn+T' three phase region exists, and the stable Al+Zn+CuZn4 three phase region dosen't in Al-Zn-Cu system at room temperature with experiment of SEM, EPMA and XRD.
利用扫描电镜、电子探针和X射线衍射实验确定了Al-Zn-Cu系在室温下存在稳态Al+Zn+T＇三相区,而不存在稳态的Al+Zn+CuZn4三相区。
补充资料：Cu-Zn-Al shape memory alloy
分子式：
CAS号：
性质：一种含Zn l8％～37％(质量)、Al 2％～8％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在93～373K之间。其形状记忆应变约4％。该合金一般在大气或真空感应炉中熔炼，采用石墨或氧化铝坩埚。该合金易于冷热加工，如将其加热到(α+β)两相区，缓冷后得到两相组织，亦可进行冷拉。为了使合金形状记忆效应稳定，可以在423～473K油浴中进行等温淬火或一般淬火后在373K进行时效处理。该合金晶粒比较粗大，可加入微量元素V、B、Ti等使晶粒细化。
CAS号：
性质：一种含Zn l8％～37％(质量)、Al 2％～8％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在93～373K之间。其形状记忆应变约4％。该合金一般在大气或真空感应炉中熔炼，采用石墨或氧化铝坩埚。该合金易于冷热加工，如将其加热到(α+β)两相区，缓冷后得到两相组织，亦可进行冷拉。为了使合金形状记忆效应稳定，可以在423～473K油浴中进行等温淬火或一般淬火后在373K进行时效处理。该合金晶粒比较粗大，可加入微量元素V、B、Ti等使晶粒细化。