1) Al-Zn-Mg-Cu alloy
Al-Zn-Mg-Cu 合金
2) Al-Zn-Mg-Cu alloy
Al-Zn-Mg-Cu合金
1.
Research on grain stability under room temperature of nanocrystalline Al-Zn-Mg-Cu alloy cryomilled powders;
液氮球磨Al-Zn-Mg-Cu合金纳米晶粉末的室温稳定性研究
2.
Effects of Zr on Microstructure and Properties of Al-Zn-Mg-Cu Alloy;
Zr对Al-Zn-Mg-Cu合金组织和性能的影响
3.
Effect of copper content on the properties and fracture behavior in Al-Zn-Mg-Cu alloys;
Cu含量对Al-Zn-Mg-Cu合金的组织性能和断裂行为的影响
3) Al-Zn-Cu-Mg-Zr alloy
Al-Zn-Cu-Mg-Zr合金
4) Al-Zn-Li-Mg-Cu alloy
Al-Zn-Li-Mg-Cu合金
5) Al-Zn-Mg-Cu-Cr alloy
Al-Zn-Mg-Cu-Cr合金
1.
Structures refinement of Al-Zn-Mg-Cu-Cr alloy thick plates;
Al-Zn-Mg-Cu-Cr合金厚板组织细化
6) Al-Zn-Mg-Cu-Li alloy
Al-Zn-Mg-Cu-Li合金
1.
DSC (Differential Scanning Calorimetric) techniques were used to investigate the kinetics of microstructure transformation of Al-Zn-Mg-Cu-Li alloy during aging at 393 K, 24 anId 393 K, 3.
采用差热法(DSC)对Al-Zn-Mg-Cu-Li合金在393K,24h和393K,3。
补充资料：Cu-Zn-Al shape memory alloy
分子式：
CAS号：
性质：一种含Zn l8％～37％(质量)、Al 2％～8％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在93～373K之间。其形状记忆应变约4％。该合金一般在大气或真空感应炉中熔炼，采用石墨或氧化铝坩埚。该合金易于冷热加工，如将其加热到(α+β)两相区，缓冷后得到两相组织，亦可进行冷拉。为了使合金形状记忆效应稳定，可以在423～473K油浴中进行等温淬火或一般淬火后在373K进行时效处理。该合金晶粒比较粗大，可加入微量元素V、B、Ti等使晶粒细化。
CAS号：
性质：一种含Zn l8％～37％(质量)、Al 2％～8％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在93～373K之间。其形状记忆应变约4％。该合金一般在大气或真空感应炉中熔炼，采用石墨或氧化铝坩埚。该合金易于冷热加工，如将其加热到(α+β)两相区，缓冷后得到两相组织，亦可进行冷拉。为了使合金形状记忆效应稳定，可以在423～473K油浴中进行等温淬火或一般淬火后在373K进行时效处理。该合金晶粒比较粗大，可加入微量元素V、B、Ti等使晶粒细化。