1)  Ni-Zn ferrite
Ni-Zn 铁氧体
1.
Nanostructured Ni-Zn ferrite was successfully prepared by spraying-coprecipitation method.
采用喷射-沉淀法成功地制备了纳米晶 Ni-Zn 铁氧体粉料。
2)  Ni-Zn ferrite
Ni-Zn铁氧体
1.
Formation of nanocrystalline spinel Ni-Zn ferrite by mechanical alloying;
用机械合金化方法制备纳米晶Ni-Zn铁氧体
2.
Domain wall motion research in Ni-Zn ferrite under constant rate of H ;
匀速加场下Ni-Zn铁氧体DW运动的描述
3.
Through the calculation and analysis of -H curves with different composition and different rate of H in room temperature,some important magnetic capability parameters have been measured in Ni-Zn ferrite of medical devices.
本文通过对室温下不同成分Ni-Zn铁氧体样品在不同加场速率下的M·-H曲线计算分析,测得了医疗设备中常用的Ni-Zn铁氧体软磁材料的多项重要磁性能参数值;在无恰当积分器时,用本方法测定这些参数是可行的。
3)  Ni-Zn-Co ferrite films
Ni–Zn铁氧体薄膜
4)  Ni-Zn ferrite films
Ni-Zn铁氧体薄膜
1.
Ni-Zn ferrite films with thickness of 1-2μm were prepared by spin-spray plating method at 90℃ on glass substrates from the deoxidizing solution of FeCl2+NiCl2+ZnCl2 and the oxidizing solution of CH3COONH4+ NH3H2O+NaNO2.
用FeCl2+NiCl2+ZnCl2组成的还原液和CH3COONH4+NH3H2O+NaNO2组成的氧化液不断地向转盘上的玻璃基片喷镀,在90℃下反应制备了厚度1~2μm的Ni-Zn铁氧体薄膜。
5)  Ni-Zn soft ferrites
Ni-Zn软磁铁氧体
1.
The development and research of Ni-Zn soft ferrites were described.
本文主要阐述了Ni-Zn软磁铁氧体材料的发展和研究现状。
6)  N1-Zn-Cu ferrite
Ni-Zn-Cu铁氧体
参考词条
补充资料：Ni-Zn ferrite
分子式：
分子量：
CAS号：

性质：高频软磁铁氧体，具有尖晶石结构，由铁、镍、锌的氧化物及其盐类用陶瓷工艺制成。其电阻率较高，可用到几百兆赫。此材料可制成中频变压器、短波天线棒、磁头、磁芯。还可在高频强磁场下用作发射机终端的级间耦合变压器或质子同步加速器的谐振腔的加速磁体等。