1) high titanium sinter
高钛型烧结矿
2) V-bearing titaniferous magnetite sinter
钒钛烧结矿
1.
7% is reason- able in the V-bearing titaniferous magnetite sinter.
针对攀钢烧结生产的情况,在实验室进行了MgO对钒钛烧结矿产、质量影响的试验研究。
3) vanadium-titanium sinter
钒钛烧结矿
1.
Pointed to the statue of many influence factors and lower strength of vanadium-titanium sintering, the prediction model that is provided with markednees of test effect have been established.
针对钒钛烧结矿强度影响因素多,强度低的状况,采用多元非线性回归建立了预报模型,检验效果显著,结果显示回归值与实际值曲线拟合得很好,预报结果达到生产要求。
2.
Through laboratory test work,the effect of FeO content on the yield and quality of sinter was investigated and the reasonable value of the FeO content in vanadium-titanium sinter was presented.
通过实验室试验研究 ,分析讨论了FeO含量对攀钢钒钛烧结矿产、质量的影响 ,并提出了FeO含量的适宜值。
4) sintering of sefstromite
钒钛矿烧结
5) vanadic-titanomagnetite sintering
钒钛磁铁矿烧结
6) vanadium-titanium sinter quality
钒钛烧结矿质量
补充资料：高碱度烧结矿
高碱度烧结矿
high basicity sinter
gaojiandu shaojiekuang高碱度烧结矿(high basieity sinter)碱度(Cao/SiO:)为1.6以上的烧结矿。碱度超过2.5时，则称超高碱度烧结矿。它的含铁矿物为磁铁矿、赤铁矿，私结相矿物主要是铁酸一钙、铁酸二钙，以及少量硅酸二钙和硅酸三钙。高碱度烧结矿机械强度高、粉末少、粒度均匀、还原性好、高温冶金性能好、可落地贮存。 (1)机械强度高、粉末少。高碱度烧结矿主要含有机械强度高、还原性好的私结相矿物铁酸一钙，它在微观上与含铁矿物组成熔蚀或交织结构，勃结牢固。此外，总私结相量也高于自熔性烧结矿和熔剂性烧结矿。但当烧结高硅(5102>8%一10%)含铁原料时，即使烧结矿的碱度已达到1.6，但没有生成足够的铁酸一钙，由于正硅酸钙大量存在，仍有严重的自然粉化。欲获得机械强度好、粉末少的烧结矿，其碱度值应通过具体实验来确定。一般采用低硅(S 1024%~5%)铁料烧结时，碱度达到1.8~2.0即可得到机械强度高、粉末少的高碱度烧结矿。 (2)粒度均匀、还原性好。生产高碱度烧结矿时，烧结料中配入数量较多的熔剂，在烧结过程中可使私结相量增加，加上熔剂的分解，大量气体逸出，使烧结块微观结构上熔融充分、私结较好，而在宏观结构上出现大孔薄壁结构，经过破碎及多次转运，就成为粒度均匀、气孔率高、机械强度好的烧结小块。此外，由于钻结相矿物为易还原的铁酸一钙所组成，且气孔率高，因而还原性良好。 (3)高温冶金性能好。高碱度烧结矿，脉石熔点高、游离FeZO3减少、软熔性和低温还原粉化性都比自熔性烧结矿好。 (4)可落地贮存。高碱度烧结矿由于机械强度高、粉末少，不易自然粉化，因此允许短期落地贮存，以缓冲高炉检修与烧结继续生产的矛盾。 高炉使用高碱度烧结矿，有利于高炉强化生产、增加产量，降低焦比。高碱度烧结矿的缺点是含铁量有所下降(但这可由它的冶金性能的改善和减少直接入炉的熔剂量而得到补偿)，烧结脱硫率降低，使其含硫量上升。 生产高碱度烧结矿的工艺要求与普通烧结矿相同，但应尽量选用品位高、含硫低的原料，加强熔剂的破碎，针对原料特点以及高炉合理炉料结构的要求，通过试验研究，选择最佳的烧结矿碱度，以保证获得应有的良好性能。 (蔡汝卓周取定)