1) anatase structure
锐钛矿型结构
1.
The TiO_2 nanocryatallite hydrosol with anatase structure has been synthesized via a facile low-temperature erfluxing process with hy- drolyzation/crystallization at a temperature of 110-150℃ for 3～12 h,employing TiCl_3,TiCl_4,H_2O_2 and NaOH as the raw materials.
结果是:XRD 图表明该 TiO_2纳米晶具有锐钛矿型结构且结晶较好; TEM 图显示其颗粒均匀且粒度分布在10～30nm,集中于20nm;激光粒度分析为20nm,与 TEM 图相一致;由低温氮气吸附- 脱附实验求得其 BET 比表面积为256。
3) anatase
[英]['ænə,teis] [美]['ænə,tes]
锐钛矿型
1.
In-situ growth of anatase nano-TiO_2 on cotton fabric and its UV screening property;
锐钛矿型纳米TiO_2在棉织物上的原位生长及其抗紫外线性能
2.
One-step Synthesis of Anatase-Crystalline Titania Hollow Spheres in Aqueous Solution;
水相一步合成锐钛矿型二氧化钛空心球
3.
Then anatase nano-TiO2 powder was calcined at the temperature between 400~1 000 ℃.
在400～1 000℃之间对锐钛矿型TiO2进行煅烧,分析了不同温度处理后样品的晶体结构和光催化活性的变化。
5) anatase TiO_2
锐钛矿型TiO2
1.
We have calculated the optical properties of anatase TiO_2 and anatase TiO_2 by N-doping by plane-wave pseudo-potential method(PWP),namely the imaginary part of dielectric function ε_2(ω),the optical absorption coefficient I(ω)and the reflectivity R(ω).
用平面波赝势方法(PWP)计算了N掺杂锐钛矿型TiO2前后的光学特性,即介电函数虚部ε2(ω),光学吸收系数I(ω)和反射率R(ω)。
2.
First-principles study of the electronic structure of N-doping anatase TiO_2;
为了研究N掺杂对锐钛矿型TiO2电子结构的影响,进而揭示N掺杂导致锐钛矿型TiO2的禁带宽度变小的机理,对N掺杂TiO2进行了基于密度泛函理论的第一性原理研究。
6) anatase TiO 2
锐钛矿型TiO2A
补充资料：锐钛矿型钛白
分子式：
CAS号：
性质：以锐钛矿型二氧化钛为主成分的白色颜料。白色粉末二氧化钛含量95%～99%，折射率2.55，密度3.70～3.85g/cm3。吸油量20～24，着色力1300～1350。平均晶体颗粒0.14～0.15μm，比表面积10～14m2/g，莫氏硬度5.5～6，比热容0.71J/(℃·g)。耐化学品，耐高温。
CAS号：
性质：以锐钛矿型二氧化钛为主成分的白色颜料。白色粉末二氧化钛含量95%～99%，折射率2.55，密度3.70～3.85g/cm3。吸油量20～24，着色力1300～1350。平均晶体颗粒0.14～0.15μm，比表面积10～14m2/g，莫氏硬度5.5～6，比热容0.71J/(℃·g)。耐化学品，耐高温。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。