1) ultrafine grained dual phase steel
超细双相钢
2) super duplex steel
超级双相钢
3) fine-grained DP steel
细晶双相钢
4) super duplex stainless steel
超级双相不锈钢
1.
The tensile properties at 900-1300℃,as well as the deformed microstructure of the as-forged 00Cr25Ni7Mo4N super duplex stainless steel(SDSS)have been studied by thermo-mechanical simulator.
用Gleeble-3800热变形模拟试验机研究了锻态00Cr25Ni7Mo4N超级双相不锈钢在900～1300℃时的高温拉伸塑性和高温变形组织特征。
2.
The effect of the heat treatment on the dual phase scale and corrosion property of the super duplex stainless steel 00Cr25Ni7MoN have been introduced in this article.
本文介绍了热处理工艺对超级双相不锈钢00Cr25N i7Mo4N中两相的比例有影响,进而对该钢的耐腐蚀性能也造成影响的试验分析情况。
3.
The influence of rare earths on solidification structure of 00Cr25Ni7Mo4N super duplex stainless steel was studied.
研究了Ce对00Cr25Ni7Mo4N超级双相不锈钢凝固组织的影响,结果表明,随着钢中Ce含量的增加,其凝固组织中等轴晶线性比相应明显增加,Ce含量为0%,0。
5) ultra-high strength low-carbon Si-Mn dual phase steel
超高强低碳Si-Mn双相钢
6) Super Duplex Stainless Steel 00Cr25Ni7Mo4N
超级双相不锈钢00Cr25Ni7Mo4N
1.
Influence of Solution Temperature on Structure and Properties of Super Duplex Stainless Steel 00Cr25Ni7Mo4N;
固溶温度对超级双相不锈钢00Cr25Ni7Mo4N组织和性能的影响
补充资料：染料细粉及超细粉
分子式：
CAS号：
性质：非水溶性染料或不易溶染料常采用的剂型。如分散染料、还原染料等对粒度及粒度分布均有一定要求，要求相对集中，过细、过粗，均对使用有不良影响。染料生产企业对本企业的产品均作了规定。这些染料产品一般多在2μm到上到4μm范围内，如对某些分散染料要求控制在1μm左右，分散性能4～5级，还原染料也与分散染料近似，故有超细粉之称。为使染料产品达到上述细度，常采用万能粉碎机或砂磨、球磨等进行粉碎。
CAS号：
性质：非水溶性染料或不易溶染料常采用的剂型。如分散染料、还原染料等对粒度及粒度分布均有一定要求，要求相对集中，过细、过粗，均对使用有不良影响。染料生产企业对本企业的产品均作了规定。这些染料产品一般多在2μm到上到4μm范围内，如对某些分散染料要求控制在1μm左右，分散性能4～5级，还原染料也与分散染料近似，故有超细粉之称。为使染料产品达到上述细度，常采用万能粉碎机或砂磨、球磨等进行粉碎。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条