1) coarse grained austenite
粗晶奥氏体
1.
089%)microalloyed steel(HTP steel)with coarse grained austenite was quantitatively analyzed by double-hit test and field emission microscopy.
089%Nb,HTP钢)粗晶奥氏体(约800μm)中的形变诱导Nb(C,N)析出规律,结果表明,在1000—900℃温度区间变形时,随着形变温度的降低,析出开始(5%析出量)时间逐渐缩短,析出开始时间与温度关系曲线具有C曲线的特征。
2) austenitic grain coarsening tem-perature
奥氏体晶粒粗化温度
3) austenite matrix
奥氏体晶体
4) γ grain boundary
奥氏体晶界
1.
The research show that the second phase particles have strong pinning force to γ grain boundary of CGHAZ in micro-calcium steel.
结果表明,弥散分布的含钙的氧化物粒子,钉扎了焊接热循环过程中CGHAZ的奥氏体晶界迁移,限制了奥氏体晶粒的长大,获得较细的焊接CGHAZ晶粒度,进而改善了微钙钢焊接CGHAZ的强韧度。
5) austenite grain
奥氏体晶粒
1.
An improvement of the etching technique for displaying austenite grains in hull structure plate steel
船板钢奥氏体晶粒浸蚀显示方法的改进
2.
The austenite grains of the test steel are significantly refined after the microalloying process.
结果表明:经过钒-铌微合金化处理后,该钢的奥氏体晶粒得到显著细化;伴随着晶粒的细化,其冲击吸收功得到较大幅度的提高;在渗碳温度范围内长时间保温时不会发生奥氏体晶粒的异常长大;晶粒细化也使其渗碳层的组织和性能得到改善。
3.
The results show that when heating temperature is lower than 950℃,the experimental steel has a smaller grain dimension;when heating temperature is above 1100℃,the austenite grains grow rapidly.
研究了X70级管线钢在不同加热温度和不同保温时间下的奥氏体晶粒长大规律。
6) coarse Austenite
初晶奥氏体
补充资料：奥氏体-贝氏体球铁
分子式：
CAS号：
性质：又叫奥-贝球铁。基体组织为奥氏体加贝氏体组织的球墨铸铁。这类球铁硅含量一般在1.4%～3.8%。含锰量小于0.5%，与普通球铁比较硅偏高、锰偏低。通过调节化学成分与热处理获得理想的奥-贝球铁的基体组织为针状贝氏体或无碳贝氏体一富碳奥氏体。这类球铁具有优良的综合机械性能、强度高、耐磨性好、韧性好、特别是有高的缺口韧性，可代替钢，用于制作重要受力结构件，如曲轴、齿轮、凸轮轴等。
CAS号：
性质：又叫奥-贝球铁。基体组织为奥氏体加贝氏体组织的球墨铸铁。这类球铁硅含量一般在1.4%～3.8%。含锰量小于0.5%，与普通球铁比较硅偏高、锰偏低。通过调节化学成分与热处理获得理想的奥-贝球铁的基体组织为针状贝氏体或无碳贝氏体一富碳奥氏体。这类球铁具有优良的综合机械性能、强度高、耐磨性好、韧性好、特别是有高的缺口韧性，可代替钢，用于制作重要受力结构件，如曲轴、齿轮、凸轮轴等。