1) Twin austenite
孪晶奥氏体
2) austenite twin
奥氏体孪晶
1.
The austenite twins in the microstructures and fracture surfaces were observed and analyzed in 40CrNi and 37CrNi3 steels.
对40CrNi和37CrNi3钢组织和断口中出现的奥氏体孪晶进行了观察,对奥氏体孪晶在组织和断口中的形貌进行了分析,得出奥氏体孪晶对冷却时所得马氏体束的方向和奥氏体晶界成分以及断口形貌产生影响。
3) martensitic twin
马氏体孪晶
1.
The Ni-Mn-Ga crystal growth direction is along [100] with the deviation less than 5° The martensitic twins reorientation process was detected by the stress-strain curves.
沿单晶试样的3个边分别进行压缩实验,研究马氏体孪晶再取向应力应变行为。
4) twin martensite
孪晶马氏体
1.
Lowering the cooling rate leads to the decrease of the plasticity, fracture toughness and corrosion resisence of the back material, mainly due to the increase of twin martensites(including those existing in lathmartensites) after quehching.
降低淬火冷却速率，使背部材料塑性以及抗疲劳性能有一定的下降，这主要是由于淬火后孪晶马氏体（含板条内微孪晶马氏体）量有所增加，回火后，使孪晶马氏体发生退化产生脆性片状碳化物，进一步增加了回火脆
5) austenite matrix
奥氏体晶体
6) γ grain boundary
奥氏体晶界
1.
The research show that the second phase particles have strong pinning force to γ grain boundary of CGHAZ in micro-calcium steel.
结果表明,弥散分布的含钙的氧化物粒子,钉扎了焊接热循环过程中CGHAZ的奥氏体晶界迁移,限制了奥氏体晶粒的长大,获得较细的焊接CGHAZ晶粒度,进而改善了微钙钢焊接CGHAZ的强韧度。
补充资料：奥氏体-贝氏体球铁
分子式：
CAS号：
性质：又叫奥-贝球铁。基体组织为奥氏体加贝氏体组织的球墨铸铁。这类球铁硅含量一般在1.4%～3.8%。含锰量小于0.5%，与普通球铁比较硅偏高、锰偏低。通过调节化学成分与热处理获得理想的奥-贝球铁的基体组织为针状贝氏体或无碳贝氏体一富碳奥氏体。这类球铁具有优良的综合机械性能、强度高、耐磨性好、韧性好、特别是有高的缺口韧性，可代替钢，用于制作重要受力结构件，如曲轴、齿轮、凸轮轴等。
CAS号：
性质：又叫奥-贝球铁。基体组织为奥氏体加贝氏体组织的球墨铸铁。这类球铁硅含量一般在1.4%～3.8%。含锰量小于0.5%，与普通球铁比较硅偏高、锰偏低。通过调节化学成分与热处理获得理想的奥-贝球铁的基体组织为针状贝氏体或无碳贝氏体一富碳奥氏体。这类球铁具有优良的综合机械性能、强度高、耐磨性好、韧性好、特别是有高的缺口韧性，可代替钢，用于制作重要受力结构件，如曲轴、齿轮、凸轮轴等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。