1) Clay based castables
粘土质浇注料
2) clay castable
粘土浇注料
1.
Fused silica particles were added to replace clay of a similar particle size in clay castables used for coke-oven door brick.
结果表明,由于低膨胀系数熔融石英的添加,不仅降低了材料的热膨胀系数,而且因熔融石英颗粒与基质相热膨胀系数的差异在热震过程中产生了大量微裂纹,由于热膨胀系数的降低和微裂纹增韧双重作用,使得浇注料的热震稳定性明显提高;同时,添加熔融石英后粘土浇注料体积密度和显气孔率减小,因而一定程度上提高了抗热震性;但浇注料的烘后及烧后抗折强度随熔融石英添加量的增大而降低。
3) Magnesia-based castable
镁质浇注料
1.
Magnesia-based castable was prepared with the weight ratio(aggregate: fines) of 70∶30.
以高纯镁砂(8~5mm,5~3mm,3~1mm)和电熔镁砂(≤1mm)为骨料,电熔镁砂细粉、α-Al2O3微粉、亚白刚玉粉、镁铝尖晶石细粉及uf-SiO2微粉为基质,按骨料∶细粉=70∶30进行配制镁质浇注料。
2.
The relationship between the physical properties of magnesia-based castable and the technical factors for preparing the castable such as grain size composition,amount of fine powders,binder,additives,and water has been investigated.
研究镁质浇注料的各种主要工艺因素(包括骨料配比、细粉、结合剂、微粉、外加剂和成型水量)与其物理性能之间的关系,进而获得镁质浇注料的较优化组成。
3.
The direct bond magnesia-chrome bricks which have been used in burning zone of cement rotary kiln were used,making fine powder which can replace the magnesia of the magnesia-based castable.
将水泥回转窑烧成带废镁铬砖经处理后制成细粉料,用它代替镁质浇注料中的镁砂原料,研究了废镁铬砖细粉的加入对SiO2微粉结合镁质浇注料烧结性的影响。
4) Light weight castables
轻质浇注料
1.
Light weight castables were prepared using glazed hollow microsphere (addition from 40% to 60%) with low bulk density,low water absorption rate and low thermal conductivity and CA-70 high alumina cement (addition from 40% to 60%).
以体积密度小、吸水率低、热导率低的玻化微珠(加入量为40%~60%)和CA-70高铝水泥(加入量为40%~60%)为原料研制了轻质浇注料,并分别研究了玻化微珠用量对轻质浇注料常温强度、体积密度、烧后线变化率的影响。
5) magnesia castable
镁质浇注料
1.
To improve the good performance of magnesia castable,the effect of Si_3N_4 on the magnesia castable properties were studied.
为了提高镁质浇注料的耐用性,研究了Si_3N_4加入对镁质浇注料性能的影响。
2.
The slag resistance of magnesia castable without Sialon and with 5% bauxite-based β-Sialon was studied by revolution dipping meth-od at 1 600℃ for 10,15,20 and 25 minutes.
采用中频感应炉进行旋转浸渍法抗渣实验,研究了未加入和加入5%矾土基β-Sialon镁质浇注料在1600℃不同浸渍时间(分别为10,15,20,25min)条件下的抗渣性能。
6) MgO based castable materials
MgO质浇注料
1.
The effect of added quantity of MA spinel powder and α-Al 2O 3 breeze on MgO based castable materials is studied.
主要研究了MA尖晶石粉和α-Al2O3微粉加入量对MgO质浇注料性能的影响。
补充资料：粘土结合耐火浇注料
粘土结合耐火浇注料
clay bonded castable refractories
n iantu』iehe naihuo Jiaozhuliao粘土结合耐火浇注料(elay bonded castablerefractories)用软质粘土作结合剂与硅酸铝质或刚玉莫来石质等耐火骨料、粉料和外加剂配制的可浇注耐火材料。(见衬火浇注料) 分类粘土结合耐火浇注料按耐火骨料品种分为粘土质、高铝质、刚玉莫来石质和高铝轻质等。根据其性能特点又分为普通型和高强度型粘土结合耐火浇注料。 组成主要有结合剂、耐火骨料粉料和外加荆等。 结合荆选用的结合拈土因产地不同，其化学成分、物理和耐火性能也不同。作为耐火浇注料用的粘土结合剂技术要求是:A12O:占29%~35%，Fe:O:小于1.8%，RZO小于1.1%，烧失10%~14%，耐火度大于1670℃，且具有较宽的烧结温度范围。在矿物组成中，应含有少量蒙脱石和云母等物质，使其具有较好的结合性能和可塑性。粘土粉细度小于。.o88mm的应占6。环以上，其用量为7%~13%。 衬火骨抖和粉杆将缎烧合格的硅铝质熟料或刚玉莫来石经破碎或再经粉磨而制成。耐火骨料应用最、多的是粘土熟料和高铝矶土熟料，最大颗粒尺寸一般为10mm、用量为70%左右。耐火粉料为粘土耐火浇注料重要组成材料，应选择特级或一级高铝矾土熟料进行粉磨，有时也掺加氧化铝粉或刚玉粉，耐火粉料细度为小于0.o88mm的占85%以上，其用量为17%~25%。 外加荆品种较多，根据粘土结合剂的特点和施工要求，主要选用分散剂和促硬剂(见外加荆)。在粘水泥具有上述特性，又有较高的耐火性能，因为该水泥土胶体分散系中，添加碱金属离子时能形成碱离子一遇水后发生水化和水解作用，析出Ca(OH)2所盆要的粘土。因为碱离子的正电性强，电位差大，粘土微粒间时间足以满足粘土耐火浇注料的成型时间要求.同时，的斥力亦大，超过了范德华引力，即粘土的阳离子较形成的活性氧化铝与料中的二载化硅作用，在达到一多，微粒间隔增大，从而促进了粘土胶体的解胶，放出定温度时能发生二次莫来石化，也有助于改善粘土浇自由水，增强了粘土耐火浇注料的流动性，有利用于搅注料的体积稳定性和耐火性能的提高。另外，为了提高拌成型。作为粘土耐火浇注料的促硬剂，一般选用高铝粘土耐火浇注料的某些性能，有时也添加超微粉和蓝水泥或纯铝酸钙水泥，其用量为外加0.2%~3.。%。晶石等外加剂。粘土耐火浇注料混合搅拌时，两种外加剂同时添加，且性能粘土结合耐火浇注料与水泥耐火浇注料相要求在成型时保证有良好的流动性，在成型后限定的比，具有中温强度高、热态强度高、高温下体积稳定性时间内，能使耐火浇注料获得足够的强度。因此常选用好和耐剥落性强等特点。常用的粘土结合耐火浇注料迟效促硬剂，在拌和成型过程中不影响分散剂的作用，主要性能见表。成型后才逐渐使耐火浇注料发生凝聚与硬化。