1) Salt-gel reaction
盐-凝胶法
2) citrate-gel method
柠檬酸盐凝胶法
1.
Nano-maghemite with 20~30 nm particles were prepared by citrate-gel method through doping Na~(+).
用柠檬酸盐凝胶法通过掺杂钠离子制备了粒径在20~30 nm的γ-氧化铁纳米粒子。
2.
The citrate-gel method was applied to prepare nanocrystalline CoAl_2O_4 spinel powders in an attempt to reduce the temperature of preparation and the calcination times.
铝酸钴(CoAl2O4)是目前世界上最耐候、耐光、耐热、耐化学品的尖晶石型钴蓝颜料,为了解决传统钴蓝制备方法存 在的能耗高、产品粒径分布不均匀、易团聚等问题,尝试采用柠檬酸盐凝胶法合成了尖晶石型CoAl2O4纳米粉体,对样品进 行了TG-DSC、XRD、SEM等分析,考察了前驱体凝胶的热分解过程,以及煅烧温度对CoAl2O4晶化程度和粒度的影响。
3) citrate-gel process
柠檬酸盐-凝胶法
4) citrate sol-gel method
柠檬酸盐溶胶凝胶法
1.
Ultrafine W-type ferrite powders have been synthesized by citrate sol-gel method with Sr(NO3)2,Ni(NO3)2·6H2O,Fe(NO3)3·9H2O and citric acid as raw materials.
以硝酸铁、硝酸镍、硝酸锶和柠檬酸为原料,采用柠檬酸盐溶胶凝胶法合成出W型SrNi2Fe16O27铁氧体粉末。
5) citrate sol-gel process
柠檬酸盐溶胶-凝胶法
1.
BaTiO3 based powders with codopants were prepared by citrate sol-gel process.
实验着重研究了凝胶煅烧工艺制度对通过柠檬酸盐溶胶-凝胶法制备复合掺杂的BaTiO3基粉体,制备纳米粉体的影响。
2.
BaTiO_3 based powder with co-dopants were prepared by citrate sol-gel process.
通过柠檬酸盐溶胶-凝胶法制备复合掺杂的BaTiO3基粉体,着重研究了凝胶煅烧工艺制度对制备纳米粉体的影响。
3.
Using exfoliatable graphite,Fe(NO_3)_3,Co(NO_3)_2 and citric acid as raw materials,magnetic exfoliated graphite (MEG) was prepared by citrate sol-gel process.
采用柠檬酸盐溶胶-凝胶法,以可膨胀石墨、硝酸铁、硝酸钴、柠檬酸为原料制备磁性膨胀石墨,利用SEM、EDS、XRD和磁滞回线等对其微观形貌和磁性能进行了表征,研究了原料配比、可膨胀石墨的pH值及膨胀时间对磁性膨胀石墨的磁性能和油吸附性能的影响。
6) citrate sol-gel method
柠檬酸盐溶胶-凝胶法
1.
The Y-type barium ferrite Ba 2Co 2Fe 12O 22 particles were synthesized by citrate sol-gel method.
采用柠檬酸盐溶胶-凝胶法制备Y型平面六角铁氧体Ba2Co2Fe12O22。
2.
Ba-ferrite material was prepared by using citrate Sol-Gel method.
采用柠檬酸盐溶胶-凝胶法制备钡铁氧体。
补充资料：Sds-聚丙烯酰胺凝胶电泳凝胶电泳
sds-聚丙烯酰胺凝胶电泳（sds-page，sodium dodecyl sulfate-polyacrylamide gel electrohoresis）
在有去污剂十二烷基硫酸钠存在下的聚丙烯酰胺凝胶电泳。sds-page只是按照分子大小分离的，而不是根据分子所带的电荷和大小分离的。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条