1) oxalic acid as a chelating agent
草酸盐辅助溶胶-凝胶法
2) PEG-assisted sol-gel method
PEG辅助的溶胶-凝胶法
3) urea-assisted sol-gel method
尿素辅助溶胶凝胶法
4) PVA-assisted Sol-Gel method
PVA辅助溶胶-凝胶法
5) citrate sol-gel method
柠檬酸盐溶胶凝胶法
1.
Ultrafine W-type ferrite powders have been synthesized by citrate sol-gel method with Sr(NO3)2,Ni(NO3)2·6H2O,Fe(NO3)3·9H2O and citric acid as raw materials.
以硝酸铁、硝酸镍、硝酸锶和柠檬酸为原料,采用柠檬酸盐溶胶凝胶法合成出W型SrNi2Fe16O27铁氧体粉末。
6) citrate sol-gel process
柠檬酸盐溶胶-凝胶法
1.
BaTiO3 based powders with codopants were prepared by citrate sol-gel process.
实验着重研究了凝胶煅烧工艺制度对通过柠檬酸盐溶胶-凝胶法制备复合掺杂的BaTiO3基粉体,制备纳米粉体的影响。
2.
BaTiO_3 based powder with co-dopants were prepared by citrate sol-gel process.
通过柠檬酸盐溶胶-凝胶法制备复合掺杂的BaTiO3基粉体,着重研究了凝胶煅烧工艺制度对制备纳米粉体的影响。
3.
Using exfoliatable graphite,Fe(NO_3)_3,Co(NO_3)_2 and citric acid as raw materials,magnetic exfoliated graphite (MEG) was prepared by citrate sol-gel process.
采用柠檬酸盐溶胶-凝胶法,以可膨胀石墨、硝酸铁、硝酸钴、柠檬酸为原料制备磁性膨胀石墨,利用SEM、EDS、XRD和磁滞回线等对其微观形貌和磁性能进行了表征,研究了原料配比、可膨胀石墨的pH值及膨胀时间对磁性膨胀石墨的磁性能和油吸附性能的影响。
补充资料：溶胶-凝胶法
分子式：
CAS号：
性质：一种用于制取无机固体材料和器件的方法。无机固体化合物和无机材料通常是利用高温固相反应制备，但是，一般地说，高温固相反应得到固体产物的均匀性较差，反应所需的温度较高，产物的料理论基础和形貌也无法控制。溶胶-凝胶方法利用前体物（如醇盐或无机盐）将反应物在分子的尺度上均匀混合，经溶胶和凝胶过程使之转变为固体；由于固体凝胶中反应物是在分子水平上均匀混合，避免了固相反应扩散过程，使反应可以在较低的温度下进行，还可以根据需要将凝胶成型，再经热处理得到具有一定形状的材料和器件。利用溶胶-凝胶方法可以制备出各种形态的材料，如薄膜、纤维、块体或粉末等。近年来，溶胶-凝胶方法在很多领域中得到了广泛应用，特别是在陶瓷材料和器件上制造中的应用，得到了多种均匀、具有特定微结构和性能的固体材料。
CAS号：
性质：一种用于制取无机固体材料和器件的方法。无机固体化合物和无机材料通常是利用高温固相反应制备，但是，一般地说，高温固相反应得到固体产物的均匀性较差，反应所需的温度较高，产物的料理论基础和形貌也无法控制。溶胶-凝胶方法利用前体物（如醇盐或无机盐）将反应物在分子的尺度上均匀混合，经溶胶和凝胶过程使之转变为固体；由于固体凝胶中反应物是在分子水平上均匀混合，避免了固相反应扩散过程，使反应可以在较低的温度下进行，还可以根据需要将凝胶成型，再经热处理得到具有一定形状的材料和器件。利用溶胶-凝胶方法可以制备出各种形态的材料，如薄膜、纤维、块体或粉末等。近年来，溶胶-凝胶方法在很多领域中得到了广泛应用，特别是在陶瓷材料和器件上制造中的应用，得到了多种均匀、具有特定微结构和性能的固体材料。