1) hexagonal titanioferrite structure
六方钛铁矿结构
1.
The XRD and DTA demonstrate that the additive MgO stabilizes the hexagonal titanioferrite structure, avoiding the ZnTiO3 decomposes into Zn2TiO4 and rutile above 945℃.
本论文研究了微波低介介质陶瓷ZnTiO3 的六方钛铁矿结构和微波介电性能，通过XRD和DTA分析表明，添加MgO稳定了系统的六方钛铁矿结构，避免了预烧温度高于945℃时，ZnTiO3分解成Zn2TiO4和金红石。
2) hexagonal perovskite
六方类钙钛矿结构
3) ilmenite structure
钛铁矿结构
4) tetragonal perovskite structure
四方钙钛矿结构
1.
It was found that the tetragonal perovskite structure formed at 900 ℃ and the lattice parameters kept nearly the same as those of not doping with SmVO4.
XRD谱图显示,在900℃下处理的样品形成了单相稳定的四方钙钛矿结构晶体,其晶格常数比没有进行掺杂的SmVO4晶格常数略微降低,说明Sr已经很好地掺杂进入SmVO4的晶格结构中;在650~750℃,单电池最大输出功率密度为209。
5) hexagonal wurtzite structure
六方纤锌矿结构
1.
Measurement results by X-ray diffraction(XRD),Fourier transform infrared(FTIR) spectroscopy and X-ray photoelectron spectroscopy(XPS) indicate that the polycrystalline GaN films with hexagonal wurtzite structure were successfully grown on the Si(111) substrates.
结果显示所得样品为六方纤锌矿结构的GaN多晶薄膜。
补充资料：蚀变钛铁矿
分子式：
CAS号：
性质：钛铁矿的高度蚀变产物，又称蚀变钛铁矿(weathered ilmenite)。化学式TiO2·nH2O，TiO2。最高含量约94%(经验值)，密度3.5～4.5g/cm3。莫氏硬度4～5.5级。颜色为黄灰色到褐色，它实际上不是一种独立的矿物，而是隐晶质锐钛矿物、金红石、板钛矿、赤铁矿(偶尔还有榍石)的混合物，贮量不大，主要产于澳大利亚。可与钛铁矿、金红石混合成TiO2含量60%～70%的混合矿，用于生产氯化法二氧化钛颜料等。
CAS号：
性质：钛铁矿的高度蚀变产物，又称蚀变钛铁矿(weathered ilmenite)。化学式TiO2·nH2O，TiO2。最高含量约94%(经验值)，密度3.5～4.5g/cm3。莫氏硬度4～5.5级。颜色为黄灰色到褐色，它实际上不是一种独立的矿物，而是隐晶质锐钛矿物、金红石、板钛矿、赤铁矿(偶尔还有榍石)的混合物，贮量不大，主要产于澳大利亚。可与钛铁矿、金红石混合成TiO2含量60%～70%的混合矿，用于生产氯化法二氧化钛颜料等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条