1) Compound carbon aerogel electrode
复合碳气凝胶电极
2) compound aerogel
复合气凝胶电极
3) composite aerogel
复合气凝胶
1.
Metal/oxide composite aerogels can be used as catalysts because of their high specific surface area.
气凝胶 (aerogels)是一种结构可控的新型轻质纳米多孔性非晶固态材料 ,而金属 /氧化物复合气凝胶由于其高的比表面积 ,可作为高效催化剂 。
2.
Ni-rich Ni/SiO2 composite aerogels in which weight percentage of Ni could reach 60% werefirstly prepared by sol-gel process of Ni-containing tetraethyl orthosilicate (NiTEOS).
首次采用含镍硅酸乙酯（NiTEOS）进行溶胶-凝胶反应来制备高镍含量的Ni／SiO2复合气凝胶，且Ni含量可在＜60wt％的范围内任意调节。
3.
CuO(CoO,MnO)/SiO2 composite aerogels with transition metal oxides as high as 75%(in mass) were prepared by using tetraethyl orthosilicate(TEOS) and acetate of Cu,Co and Mn via the sol-gel process and ambient pressure drying technique,and the gelatination mechanism was investigated.
采用正硅酸乙酯(tetraethyl orthosilicate,TEOS)和Cu,Co,Mn的醋酸盐溶液,通过溶胶-凝胶法、常压干燥制备了过渡金属氧化物含量高达75%(质量分数)的CuO(CoO,MnO)/SiO2纳米复合气凝胶,对其成胶机理进行了分析。
4) carbon aerogel
碳气凝胶
1.
The microstructure of carbon aerogel was investigated by using electron scanning microscope(SEM),pore size distribution and electrical conductivity measurement.
探索新型纳米多孔材料碳气凝胶的微结构控制,研究常压条件下纤维增强型碳气凝胶的制备,以及催化剂浓度、质量分数、纤维表面特性、溶胶注入纤维前的老化时间等制备参数对其微结构的影响。
2.
This paper examins carbon aerogel by SEM, BET and cyclic voltammetry.
在常压条件下通过溶胶-凝胶法和碳化、活化工艺制备碳气凝胶材料。
3.
The micro structure of the porous carbon aerogels is measured by SEM and BET.
经高温碳化处理 ,将RF有机气凝胶转化为碳气凝胶 ,改变RC比和聚合单体的质量百分数 ,可控制气凝胶的粒径及孔径、密度及比表面积。
5) carbon aerogels
碳气凝胶
1.
For the first time,hydroquinone-formaldehyde aerogels have been prepared by sol-gel method and CO_2 supercritical drying,and after high temperature carbonization the carbonized carbon aerogels are obtained.
首次用溶胶-凝胶法和CO2超临界干燥技术制备了对苯二酚-甲醛有机气凝胶,并经高温碳化处理得到其碳气凝胶,测得气凝胶的比表面积由碳化前的375。
2.
In this paper, carbon aerogels are obtained through ordinary pressure drying; their structural properties are investigated.
碳气凝胶是一种新型多孔碳材料,具有比表面积大、电导率高的特点。
3.
SEM, BET and pore size distribution techniques were used to characterize the morphology and pore structure of the carbon aerogels.
研究了碳气凝胶在常压条件下的制备过程和干燥方法。
6) ZrO2-SiO2 composite aerogels
硅锆复合气凝胶
补充资料：Sds-聚丙烯酰胺凝胶电泳凝胶电泳
sds-聚丙烯酰胺凝胶电泳（sds-page，sodium dodecyl sulfate-polyacrylamide gel electrohoresis）
在有去污剂十二烷基硫酸钠存在下的聚丙烯酰胺凝胶电泳。sds-page只是按照分子大小分离的，而不是根据分子所带的电荷和大小分离的。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条