1) nanocomposite aerogel
纳米复合气凝胶
1.
Preparation and characterization of CuO(CoO,MnO)/SiO_2 nanocomposite aerogels as catalysts carrier by sol-gel process
CuO(CoO,MnO)/SiO_2纳米复合气凝胶催化剂载体的溶胶-凝胶法制备与表征
2.
Cu-rich Cu/SiO_2 nanocomposite aerogels ,in which mass fraction of Cu could reach as high as 66%, were firstly prepared by sol-gel process of Cu-containing tetraethyl orthosilicate (CuTEOS).
采用含铜硅酸乙酯(CuTEO S)进行溶胶-凝胶反应来制备高Cu含量的Cu/S iO2纳米复合气凝胶,复合气凝胶中的Cu含量可在小于66%(质量分数)的范围内调节。
3.
CuO(CoO,MnO)/SiO2 nanocomposite aerogels with transition metal-oxides as high as 75wt% were prepared from tetraethyl orthosilicate(TEOS) and acetate of Cu,Co and Mn via sol-gel process and ambient pressure drying technique.
采用正硅酸乙酯(tetraethyl orthosilicate,TEOS)和Cu、Co、Mn的醋酸盐溶液,通过溶胶-凝胶法、常压干燥制备了过渡金属氧化物含量高达75wt%的CuO(CoO,MnO)/SiO2纳米复合气凝胶。
2) Ni nanowires/silica aerogel composite
Ni纳米线/SiO_2复合气凝胶
3) nanocomposite hydrogel
纳米复合水凝胶
1.
The synthesis and characterization of doubling sensitive poly(N-isopropylacrylamide-co-2-hydroxyethyl methacrylate)/clay nanocomposite hydrogels;
温度及pH敏感共聚/粘土纳米复合水凝胶的合成与性能研究
2.
Sodium carboxymethylcellulose(CMC)/poly(N-isopropylacrylamide)(PNIPA) semi-interpenetrating(semi-IPN) hydrogel was prepared incorporating CMC into PNIPA cross-linked by clay to form a new kind of nanocomposite hydrogel CMC/PNIPA/Clay was obtained.
以无机粘土为交联剂制备了具有温度、pH双重敏感特性的羧甲基纤维素钠/聚(N-异丙基丙烯酰胺)/粘土半互穿网络纳米复合水凝胶(CMC/PNIPA/Clay semi-IPN),并通过红外和透射电镜对其结构和形态进行了表征。
3.
A new kind of poly (N-isopropylacrylamide)/clay nanocomposite hydrogel (PNIPA / Clay) was prepared using inorganic clay as a crosslinker.
以无机黏土作为交联剂制备了新型聚(N-异丙基丙烯酰胺)/黏土纳米复合水凝胶(PNIPA/Clay),对其结构、温度敏感性和消溶胀行为等进行了研究。
4) nanocomposite microgel
纳米复合微凝胶
1.
A new kind of semi-interpenetrating polymer network nanocomposite microgel composed of poly(acrylic acid) (PAAc) ,poly(N-isopropylacrylamide) (PNIPA) and clay was synthesized by a two-step method.
用两步法制备了聚丙烯酸(PAAc)/聚(N异丙基丙烯酰胺)(PNIPA)/黏土半互穿网络纳米复合微凝胶,首先以黏土为交联剂,通过无皂乳液聚合制备PNIPA微凝胶,然后在PNIPA网络内使丙烯酸发生聚合,用红外(FT-IR)和透射电镜(TEM)对其结构形态进行了表征,并对微凝胶的温度和pH敏感性进行了表征。
5) Wood-nano-SiO_2 aerogel composites
木材-纳米SiO2气凝胶复合材料
6) Wood-SiO_2-aerogel composites
木材-SiO2气凝胶纳米复合材料
补充资料：Sds-聚丙烯酰胺凝胶电泳凝胶电泳
sds-聚丙烯酰胺凝胶电泳（sds-page，sodium dodecyl sulfate-polyacrylamide gel electrohoresis）
在有去污剂十二烷基硫酸钠存在下的聚丙烯酰胺凝胶电泳。sds-page只是按照分子大小分离的，而不是根据分子所带的电荷和大小分离的。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条