1) NiO/YSZ anode substrate
NiO/YSZ阳极支撑体
2) NiO-YSZ anode
NiO-YSZ阳极
1.
Performance of NiO-YSZ anode with NiO powder synthesized by precipitation method;
沉淀法合成NiO及NiO-YSZ阳极性能
2.
The YSZ films cells fabricated on NiO-YSZ anode and NiO-SDC-YSZ anode produced open-circuit voltage of 1.
NiO-YSZ阳极和NiO-SDC-YSZ阳极支撑的YSZ薄膜电池,在800℃时的开路电压分别为1。
3) NiO/YSZ anode
NiO/YSZ阳极
1.
The NiO/YSZ anode materials made by gel-casting process is one of the hot-spot in the areas of solid oxide fuel cell(SOFC).
NiO/YSZ阳极材料最佳干燥温度是25℃,固相含量为45vol%、采用15wt%石墨作为造孔剂,在1350℃烧成的NiO/YSZ阳极与固体电解质YSZ收缩率相匹配,氢气还原后NiO/YSZ阳极在600～800℃电导率达到800S/cm,符合SOFC阳极材料电导率的要求。
4) NiO-SDC-YSZ anode
NiO-SDC-YSZ阳极
1.
The YSZ films cells fabricated on NiO-YSZ anode and NiO-SDC-YSZ anode produced open-circuit voltage of 1.
NiO-YSZ阳极和NiO-SDC-YSZ阳极支撑的YSZ薄膜电池,在800℃时的开路电压分别为1。
5) NiO/YSZ anode material
NiO/YSZ阳极材料
6) NiO/SCO anode support
Ni/SCO阳极支撑体
补充资料：多孔陶瓷支撑体膜
分子式：
CAS号：
性质：在多孔陶瓷体上附着的微孔陶瓷膜层。膜层厚度一般在几微米到几十微米，外径孔径一般为0.1～0.5μm，个别也有厚度达3～5μm、孔径10μm的。多采用氧化铝、二氧化钛和二氧化锆等作膜材料。制法是：用电机带动陶瓷支撑体旋转，当溶胶液(膜材料)滴落在支撑体上，就会迅速地敷覆到支撑体表面，待溶剂蒸发、凝胶化和干燥成膜后，经热处理而制成氧化物薄膜。现已为食品(含饮料)、医药、生物技术和环境保护等领域开发利用。
CAS号：
性质：在多孔陶瓷体上附着的微孔陶瓷膜层。膜层厚度一般在几微米到几十微米，外径孔径一般为0.1～0.5μm，个别也有厚度达3～5μm、孔径10μm的。多采用氧化铝、二氧化钛和二氧化锆等作膜材料。制法是：用电机带动陶瓷支撑体旋转，当溶胶液(膜材料)滴落在支撑体上，就会迅速地敷覆到支撑体表面，待溶剂蒸发、凝胶化和干燥成膜后，经热处理而制成氧化物薄膜。现已为食品(含饮料)、医药、生物技术和环境保护等领域开发利用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条