1) Compressive strength and Splitting tensile strength
抗压强度和劈裂抗拉强度
2) compressive strength and Split strength
抗压强度和劈裂强度
3) split-tensile strength
劈裂抗拉强度
1.
Based on the structure of machine tools,the article studies the effect of split-tensile strength with different composition of bonds.
本文针对机床构件特点，研究了粘结料成分?PC组分配比、试件尺寸对其劈裂抗拉强度的影响，并提出一些看法。
2.
For studying the split-tensile strength of roller compacted concrete(RCC) and its size effect on meso-level,the random aggregate model was used and RCC was taken as three-phase heterogeneous composites consisting of mortar smut matrix and pulverized coal ash,aggregate,smut matrix plane and bond between matrix and aggregate on meso-level.
为了从细观结构上研究碾压混凝土的劈裂抗拉强度及其尺寸效应,采用随机骨料模型,在细观层次上将碾压混凝土看成是由硬化水泥粉煤灰砂浆体、粗骨料颗粒、二者间的黏结带和砂浆层面构成的三相非均质复合材料;利用有限元方法数值模拟研究碾压混凝土的细观损伤断裂和劈裂抗拉,对其劈裂抗拉强度及其尺寸效应进行了研究。
4) splitting tensile strength
劈裂抗拉强度
1.
9kg/m3) is investigated in terms of compressive,axial compressive,and splitting tensile strength properties.
9kg/m 3)的聚丙烯纤维混凝土的抗压强度、轴心抗压强度、劈裂抗拉强度与混凝土强度等级的关系的分析,并研究了其变化规律,得出以下结论:掺加聚丙烯纤维后,纤维混凝土与普通混凝土强度之间的关系与混凝土强度等级相关。
2.
The effects of steel fiber volumetric ratio,steel fiber slenderness ratio and steel fiber type on the splitting tensile strength,axial tensile strength and axial tensile stress-strain curve of steel fiber reinforced concrete(SFRC) are studied.
研究了钢纤维体积率、钢纤维长径比、钢纤维类型对钢纤维混凝土劈裂抗拉强度、轴心抗拉强度及轴心受拉应力-应变全曲线的影响规律。
3.
Discreteness of splitting tensile strength of marble is very great and it is influenced by the factors such as heterogeneous,splitting type and size effect and so on.
大理岩劈裂抗拉强度具有较大的离散性,并受非均质性、劈裂形式及尺寸效应等多种因素影响。
5) split tensile strength
劈裂抗拉强度
1.
To investigate the effect of fiber volume fraction on mechanical properties of carbon fiber cement composite,the compressive strength and split tensile strength are tested for different fiber volume fractions.
为了研究碳纤维掺量对水泥砂浆力学性能的影响,对不同掺量下水泥砂浆的抗压强度与劈裂抗拉强度进行了测试。
2.
The varied compressive strength,flexural strength and split tensile strength of furan resin concrete of different durafiber volume content are studied.
本文主要研究了在呋喃树脂混凝土中掺入不同体积含量的杜拉纤维后,其抗压强度、抗折强度及劈裂抗拉强度的变化,给出了杜拉纤维的最佳掺量,并对杜拉纤维对呋喃树脂混凝土的增强机理进行了初步分析。
3.
The experiment focused on compressive strength,split tensile strength,flexural strength of pumice lightweight aggregate concrete of four types air content in the same water-cement ratio and dosage of cement.
对比研究了在水灰比和水泥用量不变的情况下,4种不同含气量的浮石轻骨料混凝土的抗压强度、劈裂抗拉强度和抗折强度。
6) split-tension strength
劈裂抗拉强度
1.
For studying the split-tension strength and its size effect of concrete on micro-level,the random aggregate model was used to simulate the structure of concrete,concrete is taken as three-phase composites consisting of mortar smut matrix,aggregate and bond between matrix and aggregate on micro-level.
为从细观结构上研究碾压混凝土的劈裂抗拉力学性能的尺寸效应,采用随机骨料模型模拟碾压混凝土的细观结构,在细观层次上将碾压混凝土看成是由硬化水泥砂浆体、粗骨料颗粒及二者间的黏结带构成的三相非均质复合材料;利用有限元方法数值模拟碾压混凝土的细观损伤断裂和劈裂抗拉,对其劈裂抗拉强度尺寸效应进行了研究。
补充资料：焦炭抗拉强度
焦炭抗拉强度
tensile strength of coke
、…万一万 别梦二全一幸一二一幸一一幸一; 口，MPa 图3焦炭的M20一a曲线(示例)得的200kg试验焦炉焦炭和工业焦炭的M，一。关系曲线。利用所得到的回归方程，就可能通过测得的焦炭的气孔率、视密度和显微强度预测焦炭的抗拉强度，并通过抗拉强度估计焦炭的转鼓强度。 (江中抵)蒸翼 工业焦炭实验室焦炭 然 典型弹塑性体 图2光弹性测量得到的径向压缩时试样应力分布图试样断裂，断裂时所加的力由仪器记录。有的采用恒定加载速度进行试验，一般以0.05一0.巧MN/min的加载力递增，直至试样断裂。测量也可在高温下进行，测得热态抗拉强度。试样的制作是决定抗拉强度测量准确性的最重要环节。英国规定每种焦炭取25kg。在每块完整焦炭的不同部位上，用空心钻钻取5根圆柱形焦芯，再将每根焦芯切成几根直径10一20~、长8一11mm的焦样，总共要制取50一100个焦样供试验。焦样的两个端面要相互平行并与轴向垂直，因此焦样往往需要用人工研磨。采用特制的切片机修整焦芯，不经人工研磨便可制取合格焦样。 影响因素对焦炭的抗拉强度与其他强度和微观结构参数间的关系所进行的广泛研究表明，抗拉强度与焦炭气孔率p、焦炭视密度d和焦炭显微强度限么，之间的关系符合如下回归方程: a一(A+召几州)exP(一CP)，MPa或。一(A+BM占)exp(一Cd一’)，Mpa式中A、B、c为回归常数;焦炭显微强度JUS可以用大于0.Zm。粒级的百分率」‘夕。2，也可用大于0.3mm粒级的百分率M砂“。在焦炭的抗拉强度与焦炭转鼓强度指标之间也建立了回归方程; Dz}g=100 exp(一八‘二一”)，% M:。或M:5一1 00exp(一月“，一“)，%如日本曾以220个试样得到。一0.1(11 .4J住‘，侧一114)exp(一4.2尸)，Mpa，相关系数~0.72;胡矛l一100exp(一0.81。一。G。)，%，相关系数一0.80。图3是中国测jiaotan kang】aq达ngdu焦炭抗拉强度(tensile streng小of coke)焦炭在拉力作用下断裂时，其单位面积上承受的力，即焦炭断裂时所能承受的最大拉应力，是燕炭力学性质的指标之一。焦炭属脆性材料，其断裂主要取决于拉应力。直接测定焦炭的扰拉强度十分困难，一般用径向压缩试验间接测定，所测得的值称为焦炭间接抗拉强度。1972年，英国的帕特里克(J .w.Patrick)首先测定了焦炭的间接抗拉强度(以下简称抗拉强度)。1975年，日本的宫川亚夫和藤山一郎经过进一步研究，建立了初步理论和试验方法。