2) high C-Cr cast steel
高碳铬铸钢
1.
Results show that RE and heat, treatment improves the morphology and the distribution of carbide and increases the impact toughness of high C-Cr cast steel.
研究了稀土与热处理对高碳铬铸钢碳化物的形态及冲击韧性的影响。
3) chromiuxn casting steel
高、中铬铸钢
4) high chromium cast iron
高碳高铬铸铁
1.
Microstructures of high chromium cast iron for surfacing;
高碳高铬铸铁堆焊合金组织分析
5) low carbon and high chromium cast iron
低碳高铬铸铁
1.
Based on sliding and drum wear test and microstucture examination,the influence of quenching temperature and holding time on wear resistance of low carbon and high chromium cast iron was inuvestigated.
通过滑动和滚筒式磨损试验及金相组织观察,研究了淬火温度及保温时间对低碳高铬铸铁耐磨性能的影响。
6) high-carbon medium-chromium alloy steel
高碳中铬合金钢
1.
The high-carbon medium-chromium alloy steel was austemper heat treated, and the optimum chemical composition was determined using orthogonal design.
1%C、3%~5%Cr的高碳中铬合金钢进行了等温淬火热处理,采用正交设计确定最佳化学成分配比,得到理想配合的材料韧性和硬度,将所得高碳钢与低碳钢复合铸造双金属复合衬板。
补充资料：中碳钢
分子式：
CAS号：
性质：含碳量0.25％～0.60％的碳素钢。有镇静钢、半镇静钢、沸腾钢等多种产品。除碳外还可含有少量锰(0.70％～1.20％)。按产品质量分为普通碳素结构钢和优质碳素结构钢。热加工及切削性能良好，焊接性能较差。强度、硬度比低碳钢高，而塑性和韧性低于低碳钢。可不经热处理，直接使用热轧材、冷拉材，亦可经热处理后使用。淬火、回火后的中碳钢具有良好的综合力学性能。能够达到的最高硬度约为HRC55(HB538)，σb为600～1100MPa。所以在中等强度水平的各种用途中，中碳钢得到最广泛的应用，除作为建筑材料外，还大量用于制造各种机械零件。
CAS号：
性质：含碳量0.25％～0.60％的碳素钢。有镇静钢、半镇静钢、沸腾钢等多种产品。除碳外还可含有少量锰(0.70％～1.20％)。按产品质量分为普通碳素结构钢和优质碳素结构钢。热加工及切削性能良好，焊接性能较差。强度、硬度比低碳钢高，而塑性和韧性低于低碳钢。可不经热处理，直接使用热轧材、冷拉材，亦可经热处理后使用。淬火、回火后的中碳钢具有良好的综合力学性能。能够达到的最高硬度约为HRC55(HB538)，σb为600～1100MPa。所以在中等强度水平的各种用途中，中碳钢得到最广泛的应用，除作为建筑材料外，还大量用于制造各种机械零件。