1) hexagonal perovskite
六方类钙钛矿结构
2) Hexagonal perovskite
六方类钙钛矿
1.
For the specimen calcined at 1 200 ℃,CaTiO3,La2Ti2O7 and La2TiO5 mixed phases were observed in addition to the CaLa4Ti4O15 phase,while the hexagonal perovskite single phase was achieved for the CaLa4Ti4O15 powders calcined at 1 300 ℃ or 1 400 ℃.
在1 300℃和1 400℃预烧后,获得了六方类钙钛矿CaLa4Ti4O15单相。
3) perovskite_like structure
类钙钛矿型结构
4) perovskite-like
类钙钛矿结构
1.
Preparation, Structure and Dielectric Properties of Hexagonal Layered Perovskite-like Niobate and Tantalate Ceramics;
本论文的主要目的是探索新型类钙钛矿结构的铌、钽酸盐微波介质材料。
5) tetragonal perovskite structure
四方钙钛矿结构
1.
It was found that the tetragonal perovskite structure formed at 900 ℃ and the lattice parameters kept nearly the same as those of not doping with SmVO4.
XRD谱图显示,在900℃下处理的样品形成了单相稳定的四方钙钛矿结构晶体,其晶格常数比没有进行掺杂的SmVO4晶格常数略微降低,说明Sr已经很好地掺杂进入SmVO4的晶格结构中;在650~750℃,单电池最大输出功率密度为209。
6) hexagonal titanioferrite structure
六方钛铁矿结构
1.
The XRD and DTA demonstrate that the additive MgO stabilizes the hexagonal titanioferrite structure, avoiding the ZnTiO3 decomposes into Zn2TiO4 and rutile above 945℃.
本论文研究了微波低介介质陶瓷ZnTiO3 的六方钛铁矿结构和微波介电性能，通过XRD和DTA分析表明，添加MgO稳定了系统的六方钛铁矿结构，避免了预烧温度高于945℃时，ZnTiO3分解成Zn2TiO4和金红石。
补充资料：钙钛矿型铁氧体
分子式：
CAS号：
性质：又称钙钛矿型铁氧体。具有钙钛矿型结构的铁氧体。其化学式为AFeO3(式中A为Y或一部分其他稀土元素)。其晶体结构与天然钙钛石(CaTiO3)相同，属正交晶系。具有单轴各向异性。饱和磁化强度很低，约为(4.9～11.4)×10-4T，其泡径(磁泡处于稳定状态时的直径)较大，迁移率较低。用它制作的磁泡存储器具有非挥发性、抗辐射能力强。利用薄膜技术可实现集成化，在密度与半导体存储器相同情况下功耗约可低2～3个数量级。主要用作磁泡材料。
CAS号：
性质：又称钙钛矿型铁氧体。具有钙钛矿型结构的铁氧体。其化学式为AFeO3(式中A为Y或一部分其他稀土元素)。其晶体结构与天然钙钛石(CaTiO3)相同，属正交晶系。具有单轴各向异性。饱和磁化强度很低，约为(4.9～11.4)×10-4T，其泡径(磁泡处于稳定状态时的直径)较大，迁移率较低。用它制作的磁泡存储器具有非挥发性、抗辐射能力强。利用薄膜技术可实现集成化，在密度与半导体存储器相同情况下功耗约可低2～3个数量级。主要用作磁泡材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。