1) self-reduction under high temperature
高温自还原
2) high temperature reduction
高温还原
1.
The main factors of affecting the reduction of Cr2O3 in synthetic chromite briquette by carbon at high temperature, and the condensation, growth and separating behavior of metal phase from slag phase during reduction at high temperature reduction have been researched.
研究了含碳铬矿团块在高温还原过程中影响Cr2O3还原的主要因素,以及含碳铬矿团块在高温还原过程中金属相的聚集长大及其与渣相的分离状态。
3) self-propagating high-temperature synthesis with reductive process
自蔓延高温还原合成
1.
The self-propagating high-temperature synthesis with reductive process was used to synthesize ZrB_(2)Al_(2)O_(3) composite powder.
摘 要:用自蔓延高温还原合成制备了ZrB2 Al2O3复合粉体。
4) high temperature sulfuric acid restoring
高温硫酸还原
1.
Studing the best condition of high temperature sulfuric acid restoring,the program tests the simple handicraft,during which reagent and the sources of energy are economized.
在对硫铁矿烧渣全铁含量以及组分研究的基础上,运用湿法工艺以硫铁矿烧渣为原料制备铁红,省去专用还原剂还原的步骤,研究了高温硫酸还原的最佳条件,试验确定制备铁红的简易工艺,节省了试剂与能源。
5) high temperature solution phase reduction method
高温液相还原
1.
Preparation of ultrafine cobalt powder by high temperature solution phase reduction method;
高温液相还原法制备超细钴粉末
6) high temperature solution phase reduction method
高温液相还原法
补充资料：高温氧化还原法
分子式：
CAS号：
性质：是国际原子公司研究的后处理方法，主要包括两个化学反应：氧化3UO2+O2U3O8还原 U3O8+2H23UO2+2H2O在沿元件长度每隔1～2.5cm打一个孔，在高温下氧化。氧化物体积膨胀，包壳破裂。氧化得八氧化三铀再还原成二氧化铀，如此反复三次。得到的二氧化铀氟化后再浓缩235U的含量，制成小片，烧结成片状燃料。铀在氧化、还原处理过程中得到了部分净化，部分裂变产物被去除。氙、氪、碘和铯被去除，90％钌,一半的锝、镉、铟和少量的钼和铌被去除。
CAS号：
性质：是国际原子公司研究的后处理方法，主要包括两个化学反应：氧化3UO2+O2U3O8还原 U3O8+2H23UO2+2H2O在沿元件长度每隔1～2.5cm打一个孔，在高温下氧化。氧化物体积膨胀，包壳破裂。氧化得八氧化三铀再还原成二氧化铀，如此反复三次。得到的二氧化铀氟化后再浓缩235U的含量，制成小片，烧结成片状燃料。铀在氧化、还原处理过程中得到了部分净化，部分裂变产物被去除。氙、氪、碘和铯被去除，90％钌,一半的锝、镉、铟和少量的钼和铌被去除。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。